Important acid ferrous burden properties in the cohesive zone of a blast furnace

Abstract

The high-temperature behaviour of reducing ferrous materials is quantified using a laboratory softening and melting test. Using a combination of standard, non-standard and quenched tests supported by optical image analysis this work has highlighted some important differences in behaviour between lump, pellets and sinter as well as between the lump ores and the pellets. One lump ore is denser than the other and there is also a denser pellet. In both cases, the denser ore/pellet is also higher in silica content. Densification of the ferrous bed leads to reduced bed permeability. Studies indicate that densification can happen through two mechanisms. Results show that material density and silica content are two key factors causing increased bed densification. Material density influences reduction efficiency and wustite levels while silica influences the level of fayalite formed. Fayalite is formed by reactions between wustite and silica. Results also show that the behaviour of fluxed sinter is superior to ore and acid pellets because lime preferentially reacts with silica to form dicalcium silicate, a high melting temperature compound. Studies using mixtures of fluxed sinter and lump ore indicate that blast furnace burdens can easily accommodate 20% ore.

Keywords

Ferrous materials Silica content Material porosity Softening and melting Bed densification mechanisms

Get full access to this article

View all access options for this article.

References

Bakker,

1999. Softening in the blast furnace process. PhD thesis, Delft University of Technology, Delft.

Barnaba,

1985. Influence of chemical characteristic on softening and melting-down properties of iron ore sinter. Ironmaking & Steelmaking, 12, (2), pp.53–63.

Biswas,

A. K.

1982. Principles of blast furnace iron making. Brisbane: Cootha Publ. House, pp.8, 108.

Borinder,

and Bi,

1989. Softening–melting properties of pellets under simulated blast furnace conditions. Scandinavian Journal of Metallurgy, 18, pp.280–7.

Clixby,

1980. Softening and melting of superfluxed sinters and acid pellets. Ironmaking Conference Proceedings, 39, pp.370–89 (ISS, Warrendale, PA).

Dawson,

1987. Determination of the high temperature properties of blast furnace materials. SEAISI Quarterly Journal, 16, pp.23–42.

Kaushik,

and Fruehan,

2006. Mixed burden softening and melting phenomena in blast furnace operation Part 1- X-ray observation of ferrous burden. Ironmaking & Steelmaking, 33, (6), pp.507–19. doi: 10.1179/174328106X118107

Loo,

C. E.

and Bristow,

N. J.

1998. Properties of iron bearing materials under simulated blast furnace indirect reduction conditions: Part 3 Reducibility. Ironmaking & Steelmaking, 25, (5), pp.366–73.

Loo,

C. E.

Matthews,

L. T.

and O'Dea,

D. P.

2011. Lump ore and sinter behaviour during softening and melting. ISIJ International, 51, (6), pp.930–8. doi: 10.2355/isijinternational.51.930

10.

Loo,

C. E.

Matthews,

L. T.

and Ostwald,

1992. Sintering mechanism of Western Australian pisolitic limonite. Mineral Processing and Extractive Metallurgy, Transactions of the Institution of Mining and Metallurgy: Section C, 101, pp.129–38.

11.

Nogueira,

P. F.

and Fruehan,

R. J.

2004. Blast furnace burden softening and melting phenomena: Part I. Pellet bulk interaction observation. Metallurgical and Materials Transactions B, 35, pp.829–38. doi: 10.1007/s11663-004-0077-6

12.

Ritz,

V. J.

, Kortmann,

H. A.

and Koch,

1998. Reduction, softening and melting properties of pellets, sinter lumpy ore and mixed blast furnace burden. In: ICSTI/Ironmaking Conference Proceedings. Warrendale, PA: ISS, pp.1635–54.

13.

Sasaki,

, Ono,

, Suzuki,

, Okuno,

and Yoshizawa,

1997. Formation and melt-down of softening–melting zone in blast furnace. Transactions of the Iron and Steel Institute of Japan, 17, pp.391–400.

14.

VDEh (ed.). 1995. Slag Atlas. 2nd edn. Dusseldorf: Verlag Stahleisen, GmbH, pp.79.

15.

Zhang,

Z. W.

, Hu,

X. M.

, Du,

H. J.

, Honeyands,

T. A.

and Lin,

L. Q.

2009. MAC lump properties study and plant performance at Baosteel Stainless Steel. In: Fifth International Congress on the Science and Technology of Ironmaking (ICSTI’09). Shangha: Chinese Society for Metals, pp.696–700.