The effect of adding yttria (Y2O3) up to 2 wt.% on low cement high alumina castable is studied. Castable compositions with self-flowing and vibratable consistency (distribution coefficients, q = 0.21 and 0.29) are prepared using commercial raw materials and processed as per the conventional processing route, cured at 110°C, and fired at 1000 and 1550°C. An increase in yttria content is found to improve the physical and mechanical properties of castables for all temperatures. Phase analysis confirms the formation of the yttrium aluminate phase, and microstructural evaluation at 1550°C indicates enhanced bonding between the matrix and aggregate phase resulting in better density and strength properties.
Get full access to this article
View all access options for this article.
References
1.
KakroudiMGYeugo-FogaingEHugerMet al.Influence of the thermal history on the mechanical properties of two alumina based castables. J Eur Ceram Soc. 2009;29:3197–3204.
2.
GungorACelikciogluOSahinS.The physical and mechanical properties of alumina-based ultralow cement castable refractories. Ceram Int. 2012;38:4189–4194.
3.
KumarSSarkarR.Alumina-spinel castable for steel ladles: an overview. Int J Appl Ceram Technol. 2022;20(1):410–423.
4.
KakroudiMGYeugo-FogaingEChotardGC.Effect of thermal treatment on damage mechanical behaviour of refractory castables: comparison between bauxite and andalusite aggregates. J Eur Ceram Soc. 2008;28:2471–2478.
5.
RigaudMPalcoSWangN. Spinel formation in the MgO-Al2O3 system relevant to basic castables. Proceedings of the unified international technical conference on refractories on refractories; Kyoto, Japan, UNITECR’95; 1995. p. 387–394.
6.
MaitraSDasSSenA.The role of TiO2 in the densification of low cement Al2O3–MgO spinel castable. Ceram Int. 2007;33:239–243.
7.
LuzAPConsoniLBPagliosaCet al.Mgo fumes as a potential binder for in situ spinel containing refractory castables. Ceram Int. 2018;44:15453–15463.
8.
LeeWEVieiraWZhangSet al.Castable refractory concretes. Int Mater Rev. 2001;46:145–167.
BraulioMALBittencourtLRMPandolfelliVC.Selection of binders for in situ spinel refractory castables. J Eur Ceram Soc. 2009;29:2727–2735.
11.
BraulioMALMilanezDHSakoEYet al.Expansion behavior of cement-bonded alumina-magnesia refractory castables. Am Ceram Soc Bull. 2007;86:9201–9206.
12.
SarkarRSharmaA.Study of spinel-containing high alumina castable with different cements. Interceram. 2014;63:368–371.
13.
SarkarRParijaA.Effect of alumina fines on high alumina self-flow low cement castables. Refractories World Forum. 2014;6:73–77.
14.
SinghAKSarkarR.Effect of binders and distribution coefficient on the properties of high alumina castables. J Aust Ceram Soc. 2014;50:93–98.
15.
SinghAKSarkarR.Synthesis and characterization of alumina sol and its use as binder in no cement high-alumina refractory castables. Int J Appl Ceram Technol. 2015;12:E54–E60.
16.
SinghAKSarkarR.High alumina castables: effect of alumina sols and distribution coefficients. Trans Indian Ceram Soc. 2015;74:225–231.
17.
SinghAKSarkarR.Nano mullite bonded refractory castable composition for high temperature applications. Ceram Int. 2016;42:12937–12945.
18.
SinghAKSarkarR.Development of spinel sol bonded high pure alumina castable composition. Ceram Int. 2016;42:17410–17419.
19.
SinghAKSarkarR.High alumina castables: a comparison among various sol-gel bonding systems. J Aust Ceram Soc. 2017;53:553–567.
20.
LiuLChenMXuLet al.Effect of BaO addition on densification and mechanical properties of Al2O3-MgO-CaO refractories. Metals (Basel). 2016;6:84.
21.
MaizoIGLuzAPPagliosaCet al.Boron sources as sintering additives for alumina-based refractory castables. Ceram Int. 2017;43:10207–10216.
22.
LiuYHanBZhangTet al.Effect of zirconia particle size on the properties of alumina-spinel castables. Ceram Int. 2016;42:16961–16968.
23.
BadieeSHOtrojS.Effect of nano-titania addition on the properties of high-alumina low-cement self-flowing refractory castables. Ceram-Silikaty. 2011;55:319–325.
24.
YuanWJDengCJZhuHX.Effects of TiO2 addition on the expansion behavior of alumina–magnesia refractory castables. Mater Chem Phys. 2015;162:724–733.
25.
TangHYuanWShangH.Effects of MnO additions on the properties of alumina-magnesia refractory castables. Materiali in Tehnologije. 2018;52:711–715.
26.
YinXLChenMWangNet al.Improvement of densification and mechanical properties of MgAl2O4–CaAl4O7–CaAl12O19 composite by addition of MnO, Ceram Int. 2017;43:4706–4711.
27.
GogtasCLopezHFSobolevK.Role of cement content on the properties of self-flowing Al2O3 refractory castables. J Eur Ceram Soc. 2014;34:1365–1373.
28.
KaradenizEGurcanCOzgenSet al.Properties of alumina based low-cement self flowing castable refractories. J Eur Ceram Soc. 2007;27:1849–1853.
29.
LuzAPConsoniLBPagliosaCet al.Sintering effect of calcium carbonate in high-alumina refractory castables. Ceram Int. 2018;44:10486–10497.
30.
AbbasianAROmidvar-AskaryN.Microstructural and mechanical investigation of high alumina refractory castables containing nano-titania, Ceram Int. 2019;45:287–298.
31.
GehrePWenzelCAnezirisC. G.: Investigation of shaped alumina based refractories used in slagging gasifiers, Ceram Int. 2011;37:1701–1704.
32.
ConsonniLBLuzAPPandolfelliVC.Binding additives with sintering action for high-alumina based castables. Ceram Int. 2019;45:15290–15297.
33.
ThompsonAMSoniKKChanHMet al.Dopant distributions in rare-earth-doped alumina. J Am Ceram Soc. 1997;80:373–376.
34.
KhalilNMHassanMBEwaisEMMet al.Sintering, mechanical and refractory properties of MA spinel prepared via co-precipitation and sol–gel techniques. Alloys Compd. 2010;496:600–607.
35.
PošaracMDevečerskiAVolkov-HusovićTet al.The effect of Y2O3 addition on thermal shock behavior of magnesium aluminate spinel. Sci Sinter. 2009;41:75–81.
36.
SarkarRTripathiHSGhoshA.Reaction sintering of different spinel compositions in the presence of Y2O3, Mater Lett. 2004;58:2186–2191.
37.
WangZChenJWangXet al.Effects of rare earth oxides on physical properties and coating adhering performance of magnesia refractories. J Wuhan Univ Technol Mater. 2010;33:595–598.
38.
SahinBAkselC.Developments on the mechanical properties of MgO–MgAl2O4 composite refractories by ZrSiO4–3 mol% Y2O3 addition. J Eur Ceram Soc. 2012;32:49–57.
39.
YuanWZhuQDengCet al.Effects of rare earth oxides additions on microstructure and properties of alumina-magnesia refractory castables. Ceram Int. 2017;43:6746–6750.
40.
DingerDRFunkJE.Particle packing. III: discrete versus continuous particle sizes. Interceram. 1992;41:332–334.
41.
MukhopadhyaySSenSMaitiTet al.In situ spinel bonded refractory castable in relation to co-precipitation and sol–gel derived spinel forming agents, Ceram Int. 2003;29:857–868.
42.
SinhamahapatraSDanaKMukhopadhyaySet al.Role of different rare earth oxides on the reaction sintering of magnesium aluminate spinel. Ceram Int. 2019;45:11413–11420.
43.
ChengXYuanCGreenNet al.A.: sintering mechanisms of Yttria with different additives. Ceram Int. 2013;39:4791–4799.
44.
PilliVSarkarR.Effect of spinel content on the properties of Al2O3–SiC–C based trough castable. Ceram Int. 2016;42:2969–2982.
45.
KinsmanKMMcKittrickJSluzkyEet al.Phase development and luminescence in chromium-doped yttrium aluminum garnet (YAG:Cr) phosphors. J Am Ceram Soc. 1994;77:2866–2872.
46.
GlushkovaVB.Interaction of yttrium and aluminium oxides, Inorg Mater. 1983;19:80.
47.
NeimanAYTkachenkoEVKvichkoLAet al.Conditions and macromechanism of solid-phase synthesis of yttrium aluminates, Zh. Neorg Khim. 1980;25:2340–2345.
48.
BaruahBSarkarR.Effect of Y2O3 content on densification, microstructure and mechanical properties of reaction sintered magnesium aluminate spinel. Ceram Int. 2022;49(1):755–765.