Sulphide capacity measurements of slag with MgO content up to 18 mass% were carried out at 1713, 1743 and 1773 K to obtain reliable data for the blast furnace process. In the measurement, the slag is equilibrated with copper at a controlled oxygen partial pressure for 24 h. The sulphide capacities are calculated based on the sulphur analyses for both slag and copper.
Get full access to this article
View all access options for this article.
References
1.
RichardsonFDFrinchamCJB.Sulphur in silicate and aluminate slags. J Iron Steel Inst. 1954;178:4–15.
2.
CondoAFTLindströmDSichenD.Study on the effect of aging on the ability of calcium carbide for hot metal desulfurization. Steel Res. 2016;87:1137–1143. doi: 10.1002/srin.201500278
3.
NzottaMMSichenDSeetharamanS.Sulphide capacities in some multi component slag systems. ISIJ Int. 1998;38:1770–1779. doi: 10.2355/isijinternational.38.1170
4.
CondoAFTLindströmDKojolaNet al.Study on the equilibrium of slag and hot metal at tapping with respect to sulfur. Steel Res. 2016;87:1–9. doi: 10.1002/srin.201670011
5.
OsbornEFDe VriesRCGeeKHet al.Optimum composition of blast furnace slag as deduced from liquidus data for the quaternary system CaO-MgO-Al2O3-SiO2. J Metals. 1954;200:33–45.
6.
McCafferyRCo-workers. Research on blast furnace slags. Trans AIME. 1932;100:64–85.
7.
KärsrudK.Sulphide capacities of synthetic blast furnace slags at 1500°C. Scand J Metall. 1984;13:144–150.
8.
HolbrookWFJosephTL.Relative desulfurizing powers of blast-furnace slags. Trans AIME. 1936;120:99–117.
9.
KalyanramMRMacfarlaneTGBellHB.The activity of calcium oxide in slags in the systems CaO-MgO-SiO2, CaO-Al2O3-SiO2, and CaO-MgO-Al2O3-SiO2 at 1500°C. J Iron Steel Inst. 1960;195:58–64.
10.
AbrahamKPRichardsonFD.Sulphide capacities of silicate melts – PART II. Iron Steel Res. 1960;196:313–317.
ShiCBYangXMJiaoJSet al.A sulphide capacity prediction model of CaO-SiO2-MgO-Al2O3 ironmaking slags based on the Ion and molecule coexistence theory. ISIJ Int. 2010;50:1362–1372. doi: 10.2355/isijinternational.50.1362
XinTChushaoX.et al.Sulphur distribution between CaO-SiO2-TiO2-Al2O3-MgO slag and carbon-saturated iron at 1773 K. ISIJ Int. 1995;35:367–371. doi: 10.2355/isijinternational.35.367