Effect of TiO 2 on the crystallisation behaviour of CaF 2 –CaO–Al 2 O 3 –MgO slag for electroslag remelting of Ti-containing tool steel

Abstract

The crystallisation characteristics of CaF₂–CaO–Al₂O₃–MgO slags with various TiO₂ contents from 0 to 9.73 mass% were studied using a single hot thermocouple technique, SEM-EDS and X-ray diffraction. The crystallisation mechanism of TiO₂-bearing slag was identified based on kinetic analysis. It was found that increasing TiO₂ from 0 to 6.43 mass% inhibited the crystallisation ability of electroslag remelting-type CaF₂–CaO–Al₂O₃–MgO slag, whereas further increasing TiO₂ content up to 9.73 mass% enhanced the slag crystallisation signally. When increasing TiO₂ content to 6.43 mass%, the crystalline phase shift from CaO to Ca₁₂Al₁₄O₃₂F₂ and CaTiO₃ at high temperatures. At lower temperatures, the crystalline phase change from polygonal Ca₁₂Al₁₄O₃₂F₂ to need-like CaTiO₃. Further increasing TiO₂ content to 9.73 mass%, the crystalline phase are Ca₁₂Al₁₄O₃₂F₂ and CaTiO₃ in the range of 1473–1613 K. The crystallisation of crystalline phase in the isothermal crystallisation is surface nucleation and controlled by interface reaction when TiO₂ content is lower than 6.43 mass% in the slag. It is bulk nucleation and diffusion-controlled one-dimensional growth in slag with 9.73 mass% TiO₂.