Influence of 3-aminopropyltriethoxysilane/tetraethylorthosilicate mixture pretreatment on the microstructure and corrosion resistance of zeolite coating
Restricted accessResearch articleFirst published online May, 2023
Influence of 3-aminopropyltriethoxysilane/tetraethylorthosilicate mixture pretreatment on the microstructure and corrosion resistance of zeolite coating
The influence of silane pretreatment with five different volume ratios (100/0, 75/25, 50/50, 25/75, and 0/100) of 3-aminopropyltriethoxysilane (APTES)/tetraethylorthosilicate (TEOS) on microstructure and corrosion resistance of the hydrothermal synthesized zeolite coatings on the H13 steel substrates was investigated. The surface of the zeolite coatings on the 100/0, 75/25, and 50/50 mixture of the APTES/TEOS pretreated substrates was composed of intergrown rectangular particles. Additionally, pores were observed. A 25/75 mixture of APTES/TEOS pretreatment smoothed the edges and angles of zeolite particles with gel-like materials filled in the pores. In pure TEOS pretreatment, microcracks, and much gel-like materials were observed on the zeolite coating. The electrochemical test revealed that the zeolite coating on a 50/50 mixture of the APTES/TEOS pretreated substrate exhibited the highest corrosion resistance in 3.5 wt-% NaCl solution. This was because a 50/50 mixture of APTES/TEOS pretreatment advantageously promoted development of a dense and thick gel layer, which enhanced the intergrowth of zeolite particles.
DingRG, YangHB, LiSZ, . Failure analysis of H13 steel die for high pressure die casting Al alloy. Eng Failure Anal. 2021;124:105330. doi:10.1016/j.engfailanal.2021.105330
2.
WangYJ, JiaZ, JiJJ, . Determining the wear behavior of H13 steel die during the extrusion process of pure nickel. Surf Eng. 2011;28(8):581–586.
3.
ChangSH, TangTP, TaiFC, . Effect of liquid oxy-nitriding at various temperatures on wear and molten aluminum corrosion behaviors of AISI H13 steel. Corros Sci. 2021;178:109088. doi:10.1016/j.corsci.2020.109088
4.
YuM, ShivpuriR, RappRA.Effects of molten aluminum on H13 dies and coatings. J Mater Eng Perform. 1995;4(2):175–181. doi:10.1007/BF02664111
5.
DemirH, GündüzS, ErdenA, . Influence of the heat treatment on the microstructure and machinability of AISI H13 hot work tool steel. Int J Adv Manuf Technol. 2018;95(5-8):2951–2958. doi:10.1007/s00170-017-1426-3
6.
KrellingAP, MilanJCG, Da costaCE.Tribological behaviour of borided H13 steel with different boriding agents. Surf Eng. 2015;31(8):581–587. doi:10.1179/1743294414Y.0000000423
7.
FernandesFAP, HeckSC, PiconeCA, . On the wear and corrosion of plasma nitrided AISI H13. Surf Coat Technol. 2020;381:125216. doi:10.1016/j.surfcoat.2019.125216
DingYP, LiuR, WangL, . Corrosion and wear performance of stellite alloy hardfacing prepared via laser cladding. Prot Met Phys Chem Surf. 2020;56(2):392–404. doi:10.1134/S2070205120020069
10.
YanQ, YangK, WangZD, . Surface roughness optimization and high-temperature wear performance of H13 coating fabricated by extreme high-speed laser cladding. Opt Laser Technol. 2022;149:107823. doi:10.1016/j.optlastec.2021.107823
11.
BatistaJCA, JosephMC, GodoyC, . Micro-abrasion wear testing of PVD TiN coatings on untreated and plasma nitrided AISI H13 steel. Wear. 2001;249(10-11):971–979. doi:10.1016/S0043-1648(01)00833-X
12.
ZhouZ, WangL, HeDY, . Microstructure and wear resistance of Fe-based amorphous metallic coatings prepared by HVOF thermal spraying. J Therm Spray Techn. 2010;19(6):1287–1293. doi:10.1007/s11666-010-9556-2
13.
LuXF, YangYW, WuXK, . Synthesis of corrosion-resistant MFI-type zeolite coatings by solid-conversion secondary growth without solvent. Microporous Mesoporous Mater. 2021;311:110714. doi:10.1016/j.micromeso.2020.110714
14.
PandeHB, ParikhPA.Novel application of ZSM-5 zeolite: corrosion-resistant coating in chemical process industry. J Mater Eng Perform. 2013;22(1):190–199. doi:10.1007/s11665-012-0226-z
15.
XingJ, ChenYJ, YuCY, . Microstructure and corrosion performance of zeolite/MAO-coated Al alloy. Sur Eng. 2020;36(2):167–174. doi:10.1080/02670844.2019.1627016
16.
SongD, JingXY, WangJ, . Corrosion-resistant ZSM-5 zeolite coatings formed on Mg–Li alloy by hot-pressing. Corros Sci. 2011;53(5):1732–1737. doi:10.1016/j.corsci.2011.01.047
17.
ChowG, BediRS, YanYS, . Zeolite as a wear-resistant coating. Microporous Mesoporous Mater. 2012;151:346–351. doi:10.1016/j.micromeso.2011.10.013
18.
ChenYG, ChenSY, ChenQ, . Improvement of the wear and corrosion resistance of nitrocarburized H13 steel using hydrothermal-synthesized zeolite coating. Surf Coat Technol. 2022;447:128866. doi:10.1016/j.surfcoat.2022.128866
19.
MitraA, WangZB, CaoTG, . Synthesis and corrosion resistance of high-Silica Zeolite MTW, BEA, and MFI coatings on steel and aluminum. J Electrochem. Soc. 2002;149:B472–B478. doi:10.1149/1.1507784
20.
ChangjeanWC, ChiangAST, TsaiTC.Anti-corrosion zeolite film by the dry-gel-conversion process. Thin Solid Films. 2013;529:327–332. doi:10.1016/j.tsf.2012.09.037
21.
MadhusoodanaCD, DasRN, KameshimaY, . Microwave-assisted hydrothermal synthesis of zeolite films on ceramic supports. J Mater Sci. 2006;41(5):1481–1487. doi:10.1007/s10853-006-7490-y
22.
ZhangXF, WangJQ, LiuHO, . Factors affecting the synthesis of hetero-atom zeolite Fe-ZSM-5 membrane. Sep Purif Technol. 2003;32(1–3):151–158. doi:10.1016/S1383-5866(03)00028-5
23.
KatariyaMN, JanaAK, ParikhPA.Corrosion inhibition effectiveness of zeolite ZSM-5 coating on mild steel against various organic acids and its antimicrobial activity. J Ind Eng Chem. 2013;19(1):286–291. doi:10.1016/j.jiec.2012.08.013
24.
HonkanenM, HoikkanenM, VippolaM, . Characterization of silane layers on modified stainless steel surfaces and related stainless steel–plastic hybrids. Appl Surf Sci2011;257(22):9335–9346. doi:10.1016/j.apsusc.2011.05.058
25.
HuangLY, HaoYC, ChangJeanWC, . Growth of MFI zeolite film as corrosion protection layer of aluminum alloy. Microporous Mesoporous Mater. 2015;217:71–80. doi:10.1016/j.micromeso.2015.05.045
26.
ChauJLH, TellezC, YeungKL, . The role of surface chemistry in zeolite membrane formation. J Membr Sci. 2000;164(1–2):257–275. doi:10.1016/S0376-7388(99)00214-8
27.
HuangAS, LiuQ, WangNY, . Covalent synthesis of dense zeolite LTA membranes on various 3-chloropropyltrimethoxysilane functionalized supports. J Membr Sci. 2013;437:57–64. doi:10.1016/j.memsci.2013.02.058
28.
GaleanoYM, CornagliaL, TarditiAM.NaA zeolite membranes synthesized on top of APTES-modified porous stainless steel substrates. J Membr Sci. 2016;512:93–103. doi:10.1016/j.memsci.2016.04.005
29.
HuangBX, LiuQ, CaroJ, . Iso-butanol dehydration by pervaporation using zeolite LTA membranes prepared on 3-aminopropyltriethoxysilane-modified alumina tubes. J Membr Sci. 2014;455:200–206. doi:10.1016/j.memsci.2013.12.075
30.
HuangAS, WangNY, CaroJ.Seeding-free synthesis of dense zeolite FAU membranes on 3-aminopropyltriethoxysilane-functionalized alumina supports. J Membr Sci. 2012;389:272–279. doi:10.1016/j.memsci.2011.10.036
31.
TooraniM, AlifkhazraeiM, MahdivianM, . Effective PEO/silane pretreatment of epoxy coating applied on AZ31B Mg alloy for corrosion protection. Corros Sci. 2020;169:108608. doi:10.1016/j.corsci.2020.108608
QinY, ZangJ, BaiC, . Dual functionalization of aligned silicon nanowires by APTES and nano-Ag to achieve high response to rarefied acetone at high ambient humidity. J Mater Sci: Mater Electron. 2021;32(1):908–922. doi:10.1007/s10854-020-04868-5
34.
KaradeVC, SharmaA, DhavaleRP, . APTES monolayer coverage on self-assembled magnetic nanospheres for controlled release of anticancer drug Nintedanib. Sci Rep. 2021;11(1):5674. doi:10.1038/s41598-021-84770-0
35.
CalabreseL, BonaccorsiL, ProverbioE.Corrosion protection of aluminum 6061 in NaCl solution by silane–zeolite composite coatings. J Coat Technol Res. 2012;9(5):597–607. doi:10.1007/s11998-011-9391-5
36.
WangJ.A simple, rapid and Low-cost 3-aminopropyltriethoxysilane (APTES)-based surface plasmon resonance sensor for TNT explosive detection. Anal Sci. 2021;37(7):1029–1032. doi:10.2116/analsci.20N028
37.
PlueddemannED.Silane coupling agents. New York: Plenum Press; 1991.