The WC–12Co coatings were deposited on SS 410 substrates using a high-velocity oxygen fuel (HVOF) process and the coatings were heat-treated at 750°C for 1 h in argon environment. Further, the coatings were subjected to cryogenic treatment for 1, 2, 8 and 24 h, and its influence on the reciprocating sliding wear and corrosion characteristics was studied. The structural changes in the coatings after post-treatment were assessed by X-ray diffraction analysis and Raman spectroscopy. Microhardness was improved for cryogenically treated coatings due to the α-Co transformation into ϵ-Co. Cryogenic treatment duration was not having a significant effect on the microhardness values. However, the specific wear rate was influenced by the cryogenic treatment duration. Also, corrosion resistance was increased with the increased cryogenic treatment duration. The protective layers consisting of WO3 and Co3O4 phases formed during the cryogenic treatment are attributed to the improved corrosion resistance of the coatings.
BasakAK, CelisJP, PonthiauxP, . Effect of nanostructuring and Al alloying on corrosion behaviour of thermal sprayed WC–Co coatings. Mater Sci Eng: A. 2012;558:377–385.
2.
Jalali AzizpourM, Tolouei-RadM.The effect of spraying temperature on the corrosion and wear behavior of HVOF thermal sprayed WC–Co coatings. Ceram Int. 2019;45(11):13934–13941.
3.
GovandeAR, ChandakA, SunilBR, . Carbide-based thermal spray coatings: A review on performance characteristics and post-treatment. Int J Refractory Metals Hard Mater. 2022;103:105772.
4.
GovandeAR, KatiyarJK, SunilBR, . Effect of heat treatment environment on the structural characteristics and microhardness of high velocity oxy-fuel sprayed tungsten carbide-cobalt coatings. Materialwiss Werkstofftech. 2021;52(12):1346–1354.
5.
GovandeAR, SunilBR, DumpalaR.Reciprocating sliding wear behavior of the heat-treated WC–12Co coatings. Proc Inst Mech Eng, Part J J Eng Tribol. 2022;237(4):798–807.
6.
HazraS, SabiruddinK, BandyopadhyayPP.Plasma and HVOF sprayed WC–Co coatings as hard chrome replacement solution. Surf Eng. 2012;28(1):37–43.
BhosaleDG, RathodWS.Tribo-behaviour of APS and HVOF sprayed WC–Cr3C2–Ni coatings for gears. Surf Eng. 2021;37(1):80–90.
9.
LópezAJ, RamsJ.Protection of carbon steel against molten aluminum attack and high temperature corrosion using high velocity oxygen-fuel WC–Co coatings. Surf Coat Technol. 2015;262:123–133.
10.
BouarichaS, OucheneA, LegouxJ-G.Rietveld analysis for studying the decarburisation in HVOF WC–CO coatings. Surf Eng. 2018;34(10):747–754.
11.
GhadamiF, SohiMH, GhadamiS.Effect of bond coat and post-heat treatment on the adhesion of air plasma sprayed WC–Co coatings. Surf Coat Technol. 2015;261:289–294.
12.
PicasJA, PunsetM, MenarguesS, . Microstructural and tribological studies of as-sprayed and heat-treated HVOF Cr3C2–CoNiCrAlY coatings with a CoNiCrAlY bond coat. Surf Coat Technol. 2015;268:317–324.
13.
MahmudTB, FarrokhzadMA, KhanTI.Effect of heat treatment on wear performance of nanostructured WC-Ni/Cr HVOF sprayed coatings. Tribology Online. 2017;12(1):18–28.
14.
HouGL, AnYL, ZhaoXQ, . Effect of heat treatment on wear behaviour of WC–(W,Cr)2C–Ni coating. Surf Eng. 2012;28(10):786–790.
15.
AslSK, SohiMH, HokamotoK, . Effect of heat treatment on wear behavior of HVOF thermally sprayed WC-Co coatings. Wear. 2006;260(11):1203–1208.
16.
GallegoM, ChávezSC, de la RocheJ, . Effect of heat treatment on the wet abrasion resistance of WC–10Co4Cr coatings deposited onto stainless steel by HVOF. Tribology Mater Surfaces Interfaces. 2022;16(2):168–176.
17.
GonzálezMA, RodríguezE, MojardínE, . Study of the erosive wear behaviour of cryogenically and tempered WC–CoCr coating deposited by HVOF. Wear. 2017;376-377:595–607.
18.
WangG, GuK, HuangZ, . Improving the wear resistance of as-sprayed WC coating by deep cryogenic treatment. Mater Lett. 2016;185:363–365.
19.
GovandeAR, ChandakA, SunilBR, . Microhardness and frictional characteristics of cryogenically treated carbide coatings. Mater Today Proc. 2021;47:3112–3116.
20.
BabuA, AroraHS, NairRB, . Wear behavior of microwave-annealed and cryogenically treated thermal spray coatings: a comparative evaluation. Mater Today Proc. 2020;33:5348–5353.
21.
AslSK, RabizadehT, NooriNF.The effects of heat treatment on the corrosion behavior of HVOF-sprayed WC–17 wt% Co coatings. Protect Metals Phys Chem Surf. 2019;55(5):936–941.
22.
PicasJA, PunsetM, BaileMT, . Effect of oxygen/fuel ratio on the in-flight particle parameters and properties of HVOF WC–CoCr coatings. Surf Coat Technol. 2011;205:S364–S368.
23.
MonticelliC, FrignaniA, ZucchiF.Investigation on the corrosion process of carbon steel coated by HVOF WC/Co cermets in neutral solution. Corros Sci. 2004;46(5):1225–1237.
24.
ArunnellaiappanT, BaskaranS, ArunS, . Corrosion behaviour of detonation gun sprayed cermet coatings on AA5083. Surf Eng. 2021;37(2):263–270.
25.
PishvaP, SalehiM, GolozarMA.Effect of grinding on surface characteristics of HVOF-sprayed WC–10Co–4Cr coatings. Surf Eng. 2020;36(11):1180–1189.
26.
ReddyKRRM, RamanaiahN, SarcarM.Effect of heat treatment on corrosion behavior of duplex coatings. J King Saud Univ-Eng Sci. 2017;29(1):84–90.
27.
BricínD, PrůchaV, JansaZ, . Changes in structure and corrosion resistance of cryogenically treated WC–Co cemented carbides. IOP Conf Ser: Mater Sci Eng. 2021;1193(1):1–8.
28.
CelikON, SertA, GasanH, . Effect of cryogenic treatment on the microstructure and the wear behavior of WC–Co end mills for machining of Ti6Al4V titanium alloy. Int J Adv Manuf Technol. 2018;95(5):2989–2999.
29.
YongJ, DingC.Effect of cryogenic treatment on WC–Co cemented carbides. Mater Sci Eng: A. 2011;528(3):1735–1739.
30.
KalsiNS, SehgalR, SharmaVS.Effect of tempering after cryogenic treatment of tungsten carbide–cobalt bounded inserts. Bullet Mater Sci. 2014;37(2):327–335.
31.
BonnyK, BaetsPD, PerezY, . Friction and wear characteristics of WC–Co cemented carbides in dry reciprocating sliding contact. Wear. 2010;268(11):1504–1517.
32.
ChoJE, HwangSY, KimKY.Corrosion behavior of thermal sprayed WC cermet coatings having various metallic binders in strong acidic environment. Surf Coat Technol. 2006;200(8):2653–2662.
33.
WangQ, ZhangS, ChengY, . Wear and corrosion performance of WC–10Co4Cr coatings deposited by different HVOF and HVAF spraying processes. Surf Coat Technol. 2013;218:127–136.
34.
SouzaV, NevilleA.Mechanisms and kinetics of WC–Co− Cr high velocity oxy-fuel thermal spray coating degradation in corrosive environments. J Therm Spray Technol. 2006;15(1):106–117.
35.
HongS, WuY, ZhengY, . Effect of spray parameters on the corrosion behavior of HVOF sprayed WC–Co–Cr coatings. J Mater Eng Perform. 2014;23(4):1434–1439.
36.
LillardRS, KannerGS, ButtDP.The nature of oxide films on tungsten in acidic and alkaline solutions. J Electrochem Soc. 1998;145(8):2718–2725.
37.
LekatouA, SioulasD, KarantzalisAE, . A comparative study on the microstructure and surface property evaluation of coatings produced from nanostructured and conventional WC–Co powders HVOF-sprayed on Al7075. Surf Coat Technol. 2015;276:539–556.
38.
NanJ, YangY, LinZ.Raman spectroscopic study on the surface oxide layer of AB5-type metal hydride electrodes. Electrochim Acta. 2001;46(12):1767–1772.
39.
ThummavichaiK, WangN, XuF, . In situ investigations of the phase change behaviour of tungsten oxide nanostructures. R Soc Open Sci. 2018;5(4):1–10.
40.
ClitesM, BlickleyA, CullenDA, . Chemical preintercalation synthesis approach for the formation of new layered tungsten oxides. J Mater Sci. 2022;57(16):7814–7826.
41.
LekatouA, RegoutasE, KarantzalisAE.Corrosion behaviour of cermet-based coatings with a bond coat in 0.5M H2SO4. Corros Sci.2008;50(12):3389–3400.
42.
MohrbacherH, BlanpainB, CeltsJ-P, . Raman spectroscopy on defective wear debris generated by contact vibrations. J Mater Sci Lett. 1995;14(4):279–281.