HFCVD method was used to prepare and characterize single and gradient multi-layered diamond coatings on tungsten carbide. The wear behaviour was evaluated in ambient air, against Si3N4 ceramic balls. The results demonstrated that with the increase of carbon-source concentration from 1% to 5%, the diamond surface grains gradually refined and formed crystal clusters, and the roughness (Ra) of diamond surface decreased from 62.3 to 32.54 nm. Concerning the 100, 300, and 600 nm gradient of multilayer diamond coatings, the roughness Ra was 31.3, 35.6, and 40.5 nm, respectively. The diamond film obtained with 1% CH4 concentration exhibited poor wear resistance. For higher CH4 concentration, the abrasion resistance increased gradually. The average friction coefficient of multilayer diamond coatings decreased from 0.052 to 0.023 as the modulated layer thickness increased from 100 to 600 nm. The gradient multilayer structure significantly improved the tribological behaviour.
ZhangJG, WangXC, ShenB, Effect of boron and silicon doping on improving the cutting performance of CVD diamond coated cutting tools in machining CFRP. Int J Refract Met Hard Mater. 2013;41:285–292.
5.
YuQX, ZhangJY. 从资源角度论述刀具材料的发展 [The development of tool materials from a resource perspective]. New Technol New Process. 2008;03:5–8. Chinese.
6.
WangT, ZhuangH, JiangX.One step deposition of highly adhesive diamond films on cemented carbide substrates via diamond/β-SiC composite interlayers. Appl Surf Sci. 2015;359:790–796.
WioraM, BruhneK, FloterA, Grain size dependent mechanical properties of nanocrystalline diamond films grown by hot-filament CVD. Diam Relat Mater. 2008;18(5–8):927–930.
9.
SousaVFC, SilvaFJG.Recent advances on coated milling tool technology – a comprehensive review. Coatings. 2020;10(3):235.
10.
JonesAN, AhmedW, HassanIU, Pulsed biased growth of nanocrystalline diamond by hot filament chemical vapour deposition. Surf Eng. 2004;20(3):181–185.
11.
ArumugamPU, MalsheAP, BatzerSA.Dry machining of aluminum–silicon alloy using polished CVD diamond-coated cutting tools inserts. Surf Coat Technol. 2006;200(11):3399–3403.
12.
UhlmannE, SammlerF, MeixnerM, Analysis of residual stresses and wear mechanism of HF-CVD diamond coated cemented carbide tools. Prod Eng Res Devel. 2015;9(1):99–107.
13.
WangXC, ChenSL, ShenB, Frictional and wear behavior of micro-crystalline and nano-crystalline diamond films. Adv Mat Res. 2013;797:719–724.
14.
LeeST, LinZD, JiangX.CVD diamond coatings: nucleation and growth. Mater Sci Eng R. 1999;25(4):123–154.
15.
LeiXL, ShenB, ChenS, Tribological behavior between micro- and nano-crystalline diamond films under dry sliding and water lubrication. Tribol Int. 2014;69:118–127.
16.
WeiQP, YuZM, AshfoldM, Synthesis of micro- or nano-crystalline diamond films on WC-Co substrates with various pretreatments by hot filament chemical vapor deposition. Appl Surf Sci. 2010;256(13):4357–4364.
17.
ChenNC, PuLW, SunFH, Tribological behavior of HFCVD multilayer diamond film on silicon carbide. Surf Coat Technol. 2015;272:66–71.
18.
ChenNC, AiJ, ChenYC, Multilayer strategy and mechanical grinding for smoothing CVD diamond coated defective substrate. Mater Des. 2016;103:194–200.
19.
DumpalaR, ChandranM, KumarN, Growth and characterization of integrated nano- and microcrystalline dual layer composite diamond coatings on WC–Co substrates. Int J Refract Met Hard Mater. 2013;37:127–133.
20.
YanGY, WuYH, CristeaD, Machining performance of hard-brittle materials by multi-layer micro-nano crystalline diamond coated tools. Results Phys. 2019;494:401–411.
21.
LinZ, LeMJ, HaiXP, 硬质合金刀具表面微/纳米金刚石复合涂层制备研究 [Deposition of micro / nano-structured diamond composite coating on cemented carbide cutting cool]. Machinery. 2017;46(02):6–8. Chinese.
22.
TaoW, LiX, WeiS, Deposition of diamond/β-SiC/cobalt silicide composite interlayers to improve adhesion of diamond coating on WC–Co substrates by DC-plasma assisted HFCVD. Surf Coat Technol. 2011;205(8–9):3027–3034.
23.
SilvaEL, PratasS, NetoMA, Multilayer diamond coatings applied to micro-end-milling of cemented carbide. Mat. 2021;14(12):3333.
24.
CuiYX, ShenB, SunFH.Diamond deposition on WC–Co substrate with amorphous SiC interlayer. Surf Eng. 2014;30(4):237–243.
25.
AucielloO.Science and technology of a transformational multifunctional ultrananocrystalline diamond (UNCDTM) coating. Funct Diam. 2022;1:1–24.
26.
de BarrosMI, VandenbulckeL, BléchetJJ.Influence of diamond characteristics on the tribological behaviour of metals against diamond-coated Ti–6Al–4 V alloy. Wear. 2001;249(1–2):67–77.
27.
AliM, ÜrgenM, KawashimaA.High purity diamond films synthesised by chemical vapour deposition. Surf Eng. 2012;28(10):791–795.
28.
PrawerS, Nemanich RJ.Raman spectroscopy of diamond and doped diamond. Philos Trans Royal Soc. A. 2004;362(1824):2537–2565.
29.
XuZW, HeZD, SongY, Topic review: application of Raman spectroscopy characterization in micro/nano-machining. Micromachines (Basel). 2018;9(7):361.
30.
GaydaychukA, LinnikS.Tribological and mechanical properties of diamond films synthesized with high CH4 concentration. Int J Refract Met Hard Mater. 2019;85:105057.
31.
AskariSJ.Tribological characteristics of nanocrystalline diamond films grown on titanium. Surf Eng. 2009;25(6):482–486.
32.
PrawerS, HoffmanA, StuartSA, Correlation between crystalline perfection and film purity for chemically vapor deposited diamond thin coatings grown on fused quartz substrates. J Appl Phys. 1991;69(9):6625–6631.
33.
RobinsLH, FarabaughEN, FeldmanA.Line shape analysis of the Raman spectrum of diamond coatings grown by hot-filament and microwave-plasma chemical vapor deposition. J Mater Res. 1990;5(11):2456–2468.
34.
LyonSA, NemanichRJ, JohnsonNM, Microstrain in laser-crystallized silicon islands on fused silica. Appl Phys Lett. 1982;40(4):316–318.