Zinc sulphide (ZnS) thin films were synthesised by chemical bath deposition technique without using complexing agent. A physicochemical study was realized on the growth solution composed of ZnCl2, KOH, and SC(NH2)2. The bath solution was at 60°C and pH values of 11.5, 12, and 12.5 were selected for growing the material. The species distribution diagrams, and solubility curves show that the growth mechanism requires the presence of zinc-hydroxide ions, and alkaline pH for growing the ZnS. The physicochemical properties of the samples improve as the pH of the solution increases. Samples deposited at pH=12.5 present a cubic structure (sphalerite) and bandgap energy of 3.72 eV, consistent with bulk-ZnS. For comparison, additional chemical baths were prepared by using NH3 as complexing agent; however, the properties of those samples result inferior. This methodology was validated by depositing ZnS films at 40°C without the complexing agent, obtaining similar results.
HongJ, LimD, EoYJ, Chemical bath deposited ZnS buffer layer for Cu(In,Ga)Se2 thin film solar cell. Appl Surf Sci. 2018;432 Part B:250–254. doi:10.1016/j.apsusc.2017.09.133
2.
EbrahimiS, YarmandB, NaderiN.Enhanced optoelectrical properties of Mn-doped ZnS films deposited by spray pyrolysis for ultraviolet detection applications. Thin Solid Films. 2019;676:31–41. doi:10.1016/j.tsf.2019.02.046
3.
SarmaMP, KalitaJM, WaryG.Chemically deposited ZnS thin film as potential X-ray radiation sensor. Mater Sci Semicond Process. 2017;61:131–136. doi:10.1016/j.mssp.2017.01.013
4.
ZhuH, HuangJF, WangY, Synthesis and characterisation of ZnS optical thin films through cathodic electrodeposition technique. Surf Eng. 2011;27:42–45. doi:10.1179/026708409X12490360426089
5.
KumarH, RamP, SinghM.Effect of rapid thermal annealing on optical properties of zinc sulphide thin films. Surf Eng. 2017;33:181–185. 10.1080/02670844.2016.1204130
6.
VashisthaIB, SharmaMC, SharmaSK.Post annealing treatment of zinc sulphide thin film as a buffer layer for solar cell application. Surf Eng. 2017;33:299–304. doi:10.1080/02670844.2016.1254978
7.
RavishankarS, BaluAR.Studies on ternary PbZnS films suited for optoelectronic applications. Surf Eng. 2017;33:506–511. doi:10.1080/02670844.2016.1267832
8.
SalihAT, NajimAA, MuhiMAH, Single-material multilayer ZnS as anti-reflective coating for solar cell applications. Opt Commun. 2017;388:84–89. doi:10.1016/j.optcom.2016.12.035
9.
SamadpourM.Efficient CdS/CdSe/ZnS quantum dot sensitized solar cells prepared by ZnS treatment from methanol solvent. Sol Energy. 2017;144:63–70. doi:10.1016/j.solener.2016.12.057
10.
Hernández CastilloR, AcostaM, RiechI, Study of ZnS/CdS structures for solar cells applications. Optik (Stuttg). 2017;148:95–100. doi:10.1016/j.ijleo.2017.09.002
11.
Le DonneA, CavalcoliD, MereuRA, Study of the physical properties of ZnS thin films deposited by RF sputtering. Mater Sci Semicond Process. 2017;71:7–11. doi:10.1016/j.mssp.2017.06.042
12.
YangK, GuoQ, LiH, Highly efficient sol–gel synthesis for ZnS@N, S co-doped carbon nanosheets with embedded heterostructure for sodium ion batteries. J Power Sources. 2018;402:340–344. doi:10.1016/j.jpowsour.2018.09.046
13.
PolyakovSM, KarhuE, ZamiriR, Nonlinear optical response and structural properties of MBE-grown Fe:ZnS films. Opt Mater Express. 2018;8:356–367. doi:10.1364/OME.8.000356
14.
PorkodiS, BanetoM, RavichandranK.Concomitant preparation of ZnS thin film and nanopowder forms from SILAR baths: an attempt to sort-out wastage problem. J Mater Sci: Mater Electron. 2019;30:1383–1389. doi:10.1007/s10854-018-0408-z
15.
WuS, ZhaoJ, ZhaoY, Preparation, composition, and mechanical properties of CVD polycrystalline ZnS. Infrared Phys Technol. 2019;98:23–26. doi:10.1016/j.infrared.2018.12.009
16.
MariaKH, SultanaP, AsfiaMB.Chemical bath deposition of aluminum doped zinc sulfide thin films using non-toxic complexing agent: effect of aluminum doping on optical and electrical properties. AIP Adv. 2020;10:065315. doi:10.1063/5.0011191
17.
AkhtarMS, RiazS, MehmoodRF, Surfactant and template free synthesis of porous ZnS nanoparticles. Mater Chem Phys. 2017;189:28–34. doi:10.1016/j.matchemphys.2016.12.027
18.
ManeRS, LokhandeCD.Chemical deposition method for metal chalcogenide thin films. Mater Chem Phys. 2000;65:1–31. doi:10.1016/S0254-0584(00)00217-0
19.
LiuT, KeH, ZhangH, Effect of four different zinc salts and annealing treatment on growth, structural, mechanical, and optical properties of nanocrystalline ZnS thin films by chemical bath deposition. Mater Sci Semicond Process. 2014;26:301–311. doi:10.1016/j.mssp.2014.05.003
20.
PejjaiB, Minnam ReddyVR, SekuK, Chemical bath deposition of Mn-doped ZnS thin films using greener complexing agents: effect of Mn-doping on the optical properties. Optik (Stuttg). 2017;130:608–618. doi:10.1016/j.ijleo.2016.10.083
21.
LondhePU, RohomAB, BhandGR, Effect of complexing agent on the chemically deposited ZnS thin film. J Mater Sci: Mater Electron. 2017;28:5207–5214. doi:10.1007/s10854-016-6177-7
22.
DoñaJM, HerreroJ.Process and film characterization of chemical-bath-deposited ZnS thin films. J Electrochem Soc. 1994;141:205–210, doi:10.1149/1.2054685
23.
MokiliB, FromentM, LincotD.Chemical deposition of zinc hydroxosulfide thin films from zinc (II)–ammonia–thiourea solutions. J Phys IV. 1995;5:C3-261–C3-266. doi:10.1051/jp4:1995324
24.
O'BrienP, McAleeseJ.Developing an understanding of the processes controlling the chemical bath deposition of ZnS and CdS. J Mater Chem. 1998;8:2309–2314. doi:10.1039/A804692A
25.
LiuW-L, YangC-S, HsiehS-H, Effect of deposition variables on properties of CBD ZnS thin films prepared in chemical bath of ZnSO4/SC(NH2)2/Na3C3H5O7/NH4OH. Appl Surf Sci. 2013;264:213–218. doi:10.1016/j.apsusc.2012.09.174
26.
RodríguezCA, Sandoval-PazMG, CabelloG, Characterization of ZnS thin films synthesized through a non-toxic precursors chemical bath. Mater Res Bull. 2014;60:313–332. doi:10.1016/j.materresbull.2014.08.047
27.
Sang YongP, Jeong EunP, TaewooE, Characterization of ZnS thin films grown using chemical bath deposition with three different complexing agents. J Nanosci Nanotechnol. 2018;9:6294–6299. doi:10.1166/jnn.2018.15650
28.
González-PanzoIJ, Martín-VárguezPE, OlivaAI.Physicochemical conditions for ZnS films deposited by chemical bath. J Electrochem Soc. 2014;161:D181–D189. doi:10.1149/2.067404jes
29.
González-ChanIJ, OlivaAI.Physicochemical analysis and characterization of chemical bath deposited ZnS films at near ambient temperature. J Electrochem Soc. 2016;163:D421–D427. doi:10.1149/2.0911608jes
30.
HodesG.Chemical solution deposition of semiconductors films. New York: Marcel Dekker Inc.; 2002.
31.
González-ChanIJ, González-PanzoIJ, OlivaAI.Synthesis of ZnS thin films by chemical bath: from room temperature to 90°C. J Electrochem Soc. 2017;164:D95–D103. doi:10.1149/2.1371702jes
BasharMS, MatinR, SultanaM, Effect of rapid thermal annealing on structural and optical properties of ZnS thin films fabricated by RF magnetron sputtering technique. J Theor Appl Phys. 2020;14:53–63. doi:10.1007/s40094-019-00361-5
34.
GödeF.Annealing temperature effect on the structural, optical, and electrical properties of ZnS thin films. Phys B.2011;406:1653–1659. doi:10.1016/j.physb.2010.12.033
35.
ArandharaG, BoraJ, SaikiaPK.Effect of pH on the crystallite size, elastic properties, and morphology of nanostructured ZnS thin films prepared by chemical bath deposition technique. Mater Chem Phys. 2020;241:122277, doi:10.1016/j.matchemphys.2019.122277