We report on atomic layer deposition (ALD) of Al2O3 films onto 925 silver and assess their efficiency to prevent metal scratching and tarnishing. Films of five thicknesses (12, 16, 21, 25 and 31 nm) were deposited on the 925 silver. Optical characterization revealed that the colour difference of coated silver increased with film thickness, where the film thickness below 25 nm preserves the lustre of the silver. The tarnishing resistance increased with film thickness, and films thicker than 16 nm were resistant to corrosion in Na2S solution. The hardness and modulus of the film were 6.4 and 2 times that of 925 silver, respectively. Thicker films enhanced resistance to tarnishing and scratching and also led to a loss of lustre. A thickness of 25 nm was found to have an admirable combined performance. It is promising for applications of ALD process for silver protection.
SverdrupH, KocaD, RagnarsdottirKV.Investigating the sustainability of the global silver supply, reserves, stocks in society and market price using different approaches. Conserv Recyl. 2014;83:121–140. doi: 10.1016/j.resconrec.2013.12.008
2.
AngeliniE, GrassiniS, ParvisM.Silver artefacts: plasma deposition of SiOx protective layers and tarnishing evolution assessment. Corros Eng Sci Techn. 2010;45(5):334–340. doi: 10.1179/147842210X12767807773484
3.
KieserA.A “golden age” just for the living? silver vessels in tang dynasty tombs. T ang Studies. 2015;33(1):62–90. doi: 10.1179/0737503415Z.00000000015
4.
HenigMartin.The mildenhall treasure: Late roman silver plate from east anglia. J British Arch Assoc. 2017;170(1):204–207. doi: 10.1080/00681288.2017.1366722
5.
RaoCRK, PushpavanamM.Electrodeposition of platinum from platinum–ammine based baths. Trans IMF. 2006;84(2):79–82. doi: 10.1179/174591906X96049
6.
KieslerD, BastuckT, KennedyMK, Development of a high flow rate aerodynamic lens system for inclusion of nanoparticles into growing PVD films to form nanocomposite thin films. Aerosol Sci Tech. 2019;53(6):630–646. doi: 10.1080/02786826.2019.1587149
7.
KangBH, JungSJ, HongS, Improvement of the stability and optoelectronic characteristics of molybdenum disulfide thin-film transistors by applying a nitrocellulose passivation layer. J Inform Display. 2020: 1–8.
8.
YangY, LiuS, YuX, Effect of additive on zinc electrodeposition in acidic bath. Surf Eng. 2015;31(6):446–451. doi: 10.1179/1743294415Y.0000000006
9.
RenYJ, WenW, ChenJ, Corrosion behaviour of nanochromium coatings deposited by direct current magnetron sputtering. Surf Eng. 2016;32(4):294–298. doi: 10.1179/1743294415Y.0000000053
10.
AliK, DuraisamyN, KimCY, Al2O3 coatings fabrication on silver nanowires through low temperature atomic layer deposition. Mater Manuf Process. 2014;29(9):1056–1061. doi: 10.1080/10426914.2014.930959
11.
Sadeghi-TohidiFarzad, SametDavid, GrahamSamuel, Comparison of the cohesive and delamination fatigue properties of atomic-layer-deposited alumina and titania ultrathin protective coatings deposited at 200 °C. Sci Technol Adv Mat. 2014;15(1):015003. doi: 10.1088/1468-6996/15/1/015003
12.
MenegakiM, KoutivaI, KaliampakosD.Assessing the chromatic contrast in open surface excavations: a comparative study between subjective and quantitative approaches. Int J Min Reclam Env. 2015;29:112–124. doi: 10.1080/17480930.2013.866791
13.
GrissomCA, GrabowN, RileyCS, Evaluation of coating performance on silver exposed to hydrogen sulfide. J Am Inst Conserv. 2013;52:82–96. doi: 10.1179/0197136013Z.0000000007
14.
LeeYK.Comparison of CIELAB Delta E* and CIEDE2000 color-differences after polymerization and thermocycling of resin composites. Dent Mater. 2005;21(7):678–682. doi: 10.1016/j.dental.2004.09.005
15.
KoIk Jang, ParkJin, gyeong wooKim, An optically efficient full-color reflective display with an electrochromic device and color production units. J Soc Inf Display. 2019: 1–6.
16.
LangeS, ArrovalT, SaarR, Oxygen barrier properties of Al2O3- and TiO2-coated LDPE films. Polym-Plast Technol. 2015;54(3):301–304. doi: 10.1080/03602559.2014.977426
17.
YuX, ZhangX, WangCB, A tribological study of tetrahedral amorphous carbon films prepared by filtered cathodic vacuum arc technique. Vacuum. 2004;75(3):231–236. doi: 10.1016/j.vacuum.2004.03.003
18.
NayarP, KhannaA, KabirajD, Structural, optical and mechanical properties of amorphous and crystalline alumina thin films. Thin Solid Films. 2014;568(1):19–24. doi: 10.1016/j.tsf.2014.07.053
QiuL, ZhuX, HeG, The repeated spherical indentation test: an efficient way to evaluate the adhesion of hard coatings. Surf Eng. 2016;32(8):578–584. doi: 10.1080/02670844.2016.1155008