This study was conducted to investigate the current density impact on the Ni-Mo electrodeposit and on its catalytic activity of methanol oxidation in an alkaline solution. For this purpose, Ni-Mo coatings with good electrocatalytic properties were achieved by electrodeposition in the modified Watts bath containing 1-ethyl-3-methyl imidazolium bromide (EMIM [Br]) ionic liquid. The results showed that a 1–6 A dm−2 increase in the current density could decline the Mo content in the Ni-Mo/Ni coatings. The XRD patterns demonstrate that an amorphous coating formed with increasing the current density. Moreover, it was found that the catalytic performance of Ni-Mo coatings was significantly enhanced in the presence of methanol. Based on the obtained results, the Ni-Mo coating obtained at the current density of 3.5 A dm−2 and in the presence of EMIM [Br] showed a higher anodic current density, lower onset oxidation potential, and better catalytic performance.
GizM, CamaraG.The ethanol electrooxidation reaction at Pt (1 1 1): The effect of ethanol concentration. J Electroanal Chem. 2009;625(2):117–122.
2.
KowalA, GojkovićSL, LeeK-S, Synthesis, characterization and electrocatalytic activity for ethanol oxidation of carbon supported Pt, Pt–Rh, Pt–SnO2 and Pt–Rh–SnO2 nanoclusters. Electrochem commun. 2009;11(4):724–727.
3.
ZhengX, BommierC, LuoW, Sodium Metal Anodes for Room-temperature sodium-Ion Batteries: applications, Challenges and solutions. Energy Storage Materials. 2018;16:6–23.
4.
ShihZ-Y, YangZ, LinZ-H, Direct methanol fuel cells using Se/Ru core/shell cathodes provide high catalytic activity and stability. Int J Hydrogen Energy. 2011;36(12):7303–7309.
5.
JhaN, JafriRI, RajalakshmiN.Ramaprabhu S. Graphene-multi walled carbon nanotube hybrid electrocatalyst support material for direct methanol fuel cell. Int J Hydrogen Energy. 2011;36(12):7284–7290.
6.
AhmadiR.Amini MK. Synthesis and characterization of Pt nanoparticles on sulfur-modified carbon nanotubes for methanol oxidation. Int J Hydrogen Energy. 2011;36(12):7275–7283.
7.
WangL, TianC, WangH, Mass production of graphene via an in situ self-generating template route and its promoted activity as electrocatalytic support for methanol electroxidization. J Phys Chem C. 2010;114(19):8727–8733.
8.
YuanD, TanS, LiuY, Pt supported on highly graphitized lace-like carbon for methanol electrooxidation. Carbon. 2008;46(3):531–536.
9.
LamyC, LimaA, LeRhunV, Recent advances in the development of direct alcohol fuel cells (DAFC). J Power Sources. 2002;105(2):283–296.
10.
Imanian GhazanlouS, FarhoodAHS, HosouliS, Pulse and direct electrodeposition of Ni–Co/micro and nanosized SiO2 particles. Mater Manuf Processes. 2018;33(10):1067–1079.
11.
BagotzkyV, VassilievYB, KhazovaO.Generalized scheme of chemisorption, electrooxidation and electroreduction of simple organic compounds on platinum group metals. J Electroanal Chem Interfacial Electrochem. 1977;81(2):229–238.
12.
Hernández-FernándezP, MontielM, OcónP, Effect of Co in the efficiency of the methanol electrooxidation reaction on carbon supported Pt. J Power Sources. 2010;195(24):7959–7967.
13.
MontielM, Hernández-FernándezP, FierroJ, Promotional effect of upper Ru oxides as methanol tolerant electrocatalyst for the oxygen reduction reaction. J Power Sources. 2009;191(2):280–288.
14.
ZacarinMG, de BritoMM, BarbanoEP, Investigation of the Fe-Mo electrodeposition from sorbitol alkaline bath and characterization of the films produced. J Alloys Compd. 2018;750:577–586.
15.
GojkovićSL.Electrochemical oxidation of methanol on Pt3Co bulk alloy. J Serb Chem Soc. 2003;68(11):859–870.
16.
SalgadoJRC, AntoliniE, GonzalezER.Carbon supported Pt–Co alloys as methanol-resistant oxygen-reduction electrocatalysts for direct methanol fuel cells. Appl Catal, B. 2005;57(4):283–290.
17.
AntoliniE, SalgadoJR, GonzalezER.The methanol oxidation reaction on platinum alloys with the first row transition metals: the case of Pt–Co and–Ni alloy electrocatalysts for DMFCs: a short review. Appl Catal, B. 2006;63(1–2):137–149.
18.
ZengJ, LeeJY.Ruthenium-free, carbon-supported cobalt and tungsten containing binary & ternary Pt catalysts for the anodes of direct methanol fuel cells. Int J Hydrogen Energy. 2007;32(17):4389–4396.
19.
ZengJ, LeeJY.Effects of preparation conditions on performance of carbon-supported nanosize Pt-Co catalysts for methanol electro-oxidation under acidic conditions. J Power Sources. 2005;140(2):268–273.
20.
JiangJ, FengC, QianW, Effect of graphene oxide nanosheets and ultrasonic electrodeposition technique on Ni–Mo/graphene oxide composite coatings. Mater Chem Phys. 2017;199:239–248.
21.
AllahyarzadehMH, AshrafiA, GolgoonA, Effect of pulse plating parameters on the structure and properties of electrodeposited Ni-Mo films. Mater Chem Phys. 2016;175:215–222.
22.
GülH, KılıçF, AslanS, Characteristics of electro-co-deposited Ni–Al2O3 nano-particle reinforced metal matrix composite (MMC) coatings. Wear. 2009;267(5–8):976–990.
23.
ŁosiewiczB, BudniokA, RówińskiE, The structure, morphology and electrochemical impedance study of the hydrogen evolution reaction on the modified nickel electrodes. Int J Hydrogen Energy. 2004;29(2):145–157.
24.
JafarianM, MoghaddamR, MahjaniM, Electro-catalytic oxidation of methanol on a Ni–Cu alloy in alkaline medium. J Appl Electrochem. 2006;36(8):913–918.
25.
Beltowska-LehmanE, BigosA, IndykaP, Electrodeposition and characterisation of nanocrystalline Ni–Mo coatings. Surf Coat Technol. 2012;211:67–71.
26.
RogersRD, SeddonKR.Ionic liquids–solvents of the future?Science. 2003;302(5646):792–793.
27.
AllahyarzadehM, RoozbehaniB, AshrafiA.Electrodeposition of high Mo content amorphous/nanocrystalline Ni–Mo alloys using 1-ethyl-3-methyl-imidazolium chloride ionic liquid as an additive. Electrochim Acta. 2011;56(27):10210–6.
28.
ZeinE, AbedinS, EndresF.Ionic liquids: the link to high-temperature molten salts?Acc Chem Res. 2007;40(11):1106–1113.
29.
HusseyCL.Room temperature haloaluminate ionic liquids. Novel solvents for transition metal solution chemistry. Pure Appl Chem. 1988;60(12):1763–1772.
30.
WilkesJS, ZaworotkoMJ.Air and water stable 1-ethyl-3-methylimidazolium based ionic liquids. J Chem Soc, Chem Commun. 1992;13:965–967.
31.
WilliamsonGK, HallWH.X-ray line broadening from filed aluminium and wolfram. Acta Metall. 1953;1(1):22–31.
32.
ZakeriM, Yazdani-RadR, EnayatiMH, Synthesis of MoSi2–Al2O3 nanocomposite by mechanical alloying. Materials Science and Engineering: A. 2006;430(1–2):185–188.
33.
PešićO, SpasojevićM, JordovićB, Effect of electrodeposition current density on the microstructure and magnetic properties of nickel-cobalt-molybdenum alloy powders. Sci Sinter. 2014;46(1):117–127.
34.
DontenM, CesiulisH, StojekZ.Electrodeposition of amorphous/nanocrystalline and polycrystalline Ni–Mo alloys from pyrophosphate baths. Electrochim Acta. 2005;50(6):1405–1412.
35.
ZhangQ, LiZ, LinC, Glass-forming range of the Ni–Mo system derived from molecular dynamics simulation and generalized lindemann criterion. J Appl Phys. 2000;87(9):4147–4152.
36.
MousaviR, RaeissiK, SaatchiA.The effect of pH on the properties of Ni-Mo nanocrystalline electrodeposits. Int J Mod Phys B. 2008;22(18n19):3060–3068.
LiN, ChenWZ, JingBD, Preparations and properties of amorphous/nanocrystalline Ni-Mo alloy coating obtained by electrodeposition. Advan Mater Res: Trans Tech Publ. 2011;148-149:674–678.
40.
IspasA, BundA.Electrodeposition in ionic liquids. Electrochem Soc Interface. 2014;23(1):47–51.
WinandR.Electrocrystallization - theory and applications. Hydrometallurgy. 1992;29(1):567–598.
43.
WinandR.Electrocrystallization: Fundamental considerations and application to high current density continuous steel sheet plating. J Appl Electrochem. 1991;21(5):377–385.
44.
DiniJ.Electrodeposition: The Materials Science of coatings and Substrates. Westwood (NJ
): Noyes Publications; 1993.
45.
CzirákiÁ, FogarassyB, GeröcsI, Microstructure and growth of electrodeposited nanocrystalline nickel foils. J Mater Sci. 1994;29(18):4771–4777.
46.
EbrahimiF, AhmedZ.The effect of current density on properties of electrodeposited nanocrystalline nickel. J Appl Electrochem. 2003;33(8):733–739.
47.
YuanL-S, ZhengY-X, JiaM-L, Nanoporous nickel-copper-phosphorus amorphous alloy film for methanol electro-oxidation in alkaline medium. Electrochim Acta. 2015;154:54–62.
48.
Abdel AalA, HassanHB, Abdel RahimMA.Nanostructured Ni–P–TiO2 composite coatings for electrocatalytic oxidation of small organic molecules. J Electroanal Chem. 2008; 619–620:17–25.
49.
VukovićM.Voltammetry and anodic stability of a hydrous oxide film on a nickel electrode in alkaline solution. J Appl Electrochem. 1994;24(9):878–882.
50.
CuiX, GuoW, ZhouM, Promoting effect of Co in Ni m Co n (m+ n = 4) bimetallic electrocatalysts for methanol oxidation reaction. ACS Appl Mater Interfaces. 2014;7(1):493–503.
51.
FleischmannM, KorinekK, PletcherD.The oxidation of organic compounds at a nickel anode in alkaline solution. J Electroanal Chem Interfacial Electrochem. 1971;31(1):39–49.
52.
TaraszewskaJ, RosłonekG.Electrocatalytic oxidation of methanol on a glassy carbon electrode modified by nickel hydroxide formed by ex situ chemical precipitation. J Electroanal Chem. 1994;364(1–2):209–213.
53.
AllenJR, FloridoA, YoungSD, Nitrite-selective electrode based on an electropolymerized cobalt phthalocyanine. Electroanalysis. 1995;7(8):710–713.
54.
VertesG, HoranyiG.Some problems of the kinetics of the oxidation of organic compounds at oxide-covered nickel electrodes. J Electroanal Chem Interfacial Electrochem. 1974;52(1):47–53.
55.
FleischmannM, KorinekK, PletcherD.The kinetics and mechanism of the oxidation of amines and alcohols at oxide-covered nickel, silver, copper, and cobalt electrodes. J Chem Soc Perkin Trans. 1972;2(10):1396–1403.