A functionalised coating for mild steel corrosion protection was prepared in this study. A composite material SBA-15 (silicon oxide) was used as a mild steel corrosion inhibitor. The porous matrix (SBA-15) was loaded with fluconazole (F), as an inhibitor container. A sol–gel technique was used to synthesise SBA-15; and the active molecule (F) was extracted from an outdated medication using methanol as solvent. The final composite was obtained by SO2 dispersion in a methanol-F solution. The composite material was dispersed in a nitrocellulose resin, and it was characterised by X-ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Transmission Electron Microscope (TEM), Fourier Transform Infrared Spectrometry (FTIR), and physical adsorption of Nitrogen. Coatings were electrochemically evaluated by electrochemical impedance spectroscopy (EIS) tests, using a chloride/sulphate solution prepared from NaCl and (NH4)2SO4. The results demonstrated the effectiveness of the inhibitor delivery system and the consequent protection of metal against the corrosion process.
KiwilszaA, MilanowskiB, DrużbickiK, Mesoporous drug carrier systems for enhanced delivery rate of poorly water-soluble drug: nimodipine. J Porous Mater. 2015;22:817–829. doi: 10.1007/s10934-015-9955-3
2.
WangY, ZhaoQ, HuY, Ordered nanoporous silica as carriers or improved delivery of water insoluble drugs: a comparative study between three dimensional and two dimensional macroporous silica. Int J Nanomed. 2013;8:4015–4028. doi: 10.2147/IJN.S52605
3.
JinQ, QuF, JiangJ, A pH-sensitive controlled dual-drug release from meso-macroporous silica/multilayer-polyelectrolytes coated SBA-15 composites. J Sol Gel Sci Technol. 2013;66:466–471. doi: 10.1007/s10971-013-3033-6
4.
NatarajanS, SelvarajS.Mesoporous silica nanoparticles: importance of surface modifications and its role in drug delivery. RSC Adv. 2014;4:14328–14334. doi: 10.1039/c4ra00781f
5.
AndradeGF, GomideVS, da Silva JúniorAJ, An in situ synthesis of mesoporous SBA-16/hydroxyapatite for ciprofloxacin release: in vitro stability and cytocompatibility studies. J Mater Sci Mater Med. 2014;25:2527–2540. doi: 10.1007/s10856-014-5273-6
6.
Oshiro JuniorJ, Paiva AbuçafyM, Berbel ManaiaE, Drug delivery systems obtained from silica based organic-inorganic hybrids. Polymers. 2016;8:91. doi: 10.3390/polym8040091
7.
ChoiS, ChoiY, JangM, Supertough hybrid hydrogels consisting of a polymer double-network and mesoporous silica microrods for mechanically stimulated On-demand drug delivery. Adv Funct Mater. 2017;1703826:1–9.
8.
AlarcosN, SánchezF, DouhalA.Confinement effect on ultrafast events of a salicylideneaniline derivate within mesoporous metarials. Micropor Mesopor Mat. 2017;248:54–61. doi: 10.1016/j.micromeso.2017.04.011
9.
ZhangF, SunJ, BaiS, Synthesis and characterization of hollow mesoporous silica spheres with tunable shell thicknesses and its application in ibuprofen delivery. J Porous Mat. 2018;25(2):581–593. doi: 10.1007/s10934-017-0471-5
10.
dos SantosSML, NogueiraKAB, de Souza GamaM, Synthesis and characterization of ordered mesoporous silica (SBA-15 and SBA-16) for adsorption of biomolecules. Micropor Mesopor Mat. 2013;180:284–292. doi: 10.1016/j.micromeso.2013.06.043
11.
LiQ, YuH, SongJ, Synthesis of SBA-15/polyaniline mesoporous composite for removal of resorcinol from aqueous solution. Appl Surf Sci. 2014;290:260–266. doi: 10.1016/j.apsusc.2013.11.065
12.
CucinottaF, CarniatoF, PaulG, Incorporation of a semiconductive polymer into mesoporous SBA-15 platelets: toward New luminescent hybrid materials. Chem Mater. 2011;23:2803–2809. doi: 10.1021/cm103670w
13.
AzimovF, MarkovaI, StefanovaV, Synthesis and characterization of SBA-15 and Ti-SBA-15 nanoporous materials for DME catalysts. J Univ Chem Technol Metall. 2012;47:333–340.
14.
LiGL, ZhengZ, MöhwaldH, Silica/polymer double-walled hybrid nanotubes: synthesis and application as stimuli-responsive nanocontainers in self-healing coatings. ACS Nano. 2013;7:2470–2478. doi: 10.1021/nn305814q
15.
ZheludkevichML, TedimJ, FerreiraMGS.“Smart” coatings for active corrosion protection based on multi-functional micro and nanocontainers. Electrochim Acta. 2012;82:314–323. doi: 10.1016/j.electacta.2012.04.095
16.
TomićMD, DunjićB, LikićV, The use of nanoclay in preparation of epoxy anticorrosive coatings. Prog Org Coat. 2014;77:518–527. doi: 10.1016/j.porgcoat.2013.11.017
17.
RuhiG, BhandariH, DhawanSK.Designing of corrosion resistant epoxy coatings embedded with polypyrrole/SiO2 composite. Prog Org Coat. 2014;77:1484–1498. doi: 10.1016/j.porgcoat.2014.04.013
18.
BakhshandehE, JannesariA, RanjbarZ, Anti-corrosion hybrid coatings based on epoxy-silica nano-composites: toward relationship between the morphology and EIS data. Prog Org Coat. 2014;77:1169–1183. doi: 10.1016/j.porgcoat.2014.04.005
19.
HeY, XuW, TangR, pH-Responsive nanovalves based on encapsulated halloysite for the controlled release of a corrosion inhibitor in epoxy coating. RSC Adv. 2015;5:90609–90620. doi: 10.1039/C5RA19296J
20.
SnihirovaD, LamakaSV, TarybaM, Hydroxyapatite microparticles as feedback-active reservoirs of corrosion inhibitors. ACS Appl Mater Interfaces. 2010;2:3011–3022. doi: 10.1021/am1005942
21.
MontemorMF, SnihirovaDV, TarybaMG, Evaluation of self-healing ability in protective coatings modified with combinations of layered double hydroxides and cerium molibdate nanocontainers filled with corrosion inhibitors. Electrochem Acta. 2012;60:31–40. doi: 10.1016/j.electacta.2011.10.078
22.
Ávila-GonzálezC, Cruz-SilvaR, MenchacaC, Use of silica tubes as nanocontainers for corrosion inhibitor storage. Nanotechnology. 2011: 1–9.
23.
ParhizkarN, RamezanzadehB, ShahrabiT.Corrosion protection and adhesion properties of the epoxy coating applied on the steel substrate pre-treated by a sol-gel based silane coating filled with amino and isocyanate silane functionalized graphene oxide nanosheets. Appl Surf Sci. 2018;439:45–59. doi: 10.1016/j.apsusc.2017.12.240
24.
MontemorMF.Functional and smart coatings for corrosion protection: A review of recent advances. Surf Coat Technol. 2014;258:17–37. doi: 10.1016/j.surfcoat.2014.06.031
25.
Bustos-TerronesV, Menchaca-CamposC, RomeroM, Electrochemical evaluation of an outdated antifungical drug as corrosion inhibitor of mild steel in neutral chloride media. Innovations Corros Mater Sci. 2015;5:31–35.
26.
International Standard ISO 9223. Corrosion of metals and alloys – corrosivity of atmospheres – classification, determination, and estimation. Second edition; 2012.
27.
ZhaoD, YangP, MeloshN, Continuous mesoporous silica films with highly ordered large pore structures. Adv Mater. 1998;10:1380–1385. doi: 10.1002/(SICI)1521-4095(199811)10:16<1380::AID-ADMA1380>3.0.CO;2-8
28.
EsparzaJM, OjedaML, CamperoA, Development and sorption characterization of some model mesoporous and microporous silica adsorbents. J Mol Catal A Chem. 2005;228:97–110. doi: 10.1016/j.molcata.2004.09.042
29.
QinY, XiongD, LiJ, Compositions and tribological properties of PEO coatings on Ti6Al4 V alloy. Surf Eng. 2016;33(12):1–7. doi: 10.1179/1743294414Y.0000000412
Code Federal Regulations. Food and Drug Administration, Expiration Dating 21 Sec. 1995. 211-137.
32.
ParhizkarN, ShahrabiT, RamezanzadehB.A new approach for enhancement of the corrosion protection properties and interfacial adhesion bonds between the epoxy coating and steel substrate through surface treatment by covalently modified amino functionalized graphene oxide film. Corros Sci. 2017;123:55–75. doi: 10.1016/j.corsci.2017.04.011
33.
KhanmohammadiH, AllahkaramS, TowhidiN, Preparation of PEO coating on Ti6Al4 V in different electrolytes and evaluation of its properties. Surf Eng. 2016;32(6):448–456. doi: 10.1179/1743294415Y.0000000083
34.
ShubhaHN, VenkateshaTV, PavithraMK, Surface modification of mild steel by a self-assembled cetyl-trimethyl ammonium bromide (CTAB) monolayer: evaluation of its corrosion protection property. Prog Org Coat. 2016;90:267–276. doi: 10.1016/j.porgcoat.2015.10.020
35.
ZeleňákV, MaguraJ, ZeleňákováA, Carbon dioxide and methane adsorption over metal modified mesoporous SBA-15 silica. Pure Appl Chem. 2017;89(4):493–500. doi: 10.1515/pac-2016-1121
36.
WróblewskaA, MiądlickiP, Srénscek-NazzalJ, Alpha-pinene isomerization over Ti-SBA-15 catalysts obtained by the direct method: the influence of titanium content, temperature, catalyst amount and reaction time. Micropor Mesopor Mat. 2018;258:72–82. doi: 10.1016/j.micromeso.2017.09.007
37.
ThommesM, KanekoK, NeimarkAV, Physisorption of gases, with special reference to the evaluation of surface area and pore size distribution (IUPAC technical report). Pure Appl Chem. 2015;87:1051–1069. doi: 10.1515/pac-2014-1117
38.
ElhamifarD, HosseinpoorF, KarimiB, Ionic liquid-based ordered mesoporous organosilica-supported copper as a novel and efficient nanocatalyst for one-pot synthesis of biginelli products. Micropor Mesopor Mat. 2015;204:269–275. doi: 10.1016/j.micromeso.2014.11.011
39.
CheahW, SimY, YeohF.Amine-functionalized mesoporous silica for urea adsorption. Mater Chem Phys. 2016;175:151–157. doi: 10.1016/j.matchemphys.2016.03.007
40.
TomerVK, DuhanS, AdhyapakP, Mn-loades mesoporous silica nanocomposite: a highly efficient humidity sensor. J Am Ceram Soc. 2015;98(3):741–747. doi: 10.1111/jace.13383
41.
HalamováD, BadaničováM, ZeleňákV, Naproxen drug using periodic mesoporous silica SBA-15. Appl Surf Sci. 2010;256:6489–6494. doi: 10.1016/j.apsusc.2010.04.044
42.
ChangF, WangJ, LuoJ, Synthesis, characterization, and visible-light-driven photocatalytic performance of W-SBA15. J Colloid Interface Sci. 2016;468:284–291. doi: 10.1016/j.jcis.2016.01.077
43.
DugarteA, ContrerasJ, Días de DelgadoG, X-ray power diffraction data of the antifungal agents, clotrimazole and fluconazole monohydrate. Powder Diffr. 2014;29:289–294. doi: 10.1017/S0885715613001425
44.
JaroniecM, SolovyovLA.Improvement of Kruk-Jaroniec-Sayari method for pore size analysis of ordered silicas with cylindrical mesoporous. Langmuir. 2006;22:6757–6760. doi: 10.1021/la0609571
45.
HuangH, JiY, QiaoZ, Preparation, characterization, and application of magnetic Fe-SBA-15 mesoporous silica molecular sieves. J Autom Methods Manag Chem. 2010;2010: 1–7. doi: 10.1155/2010/323509
46.
ConradiM, KocijanA, Kek-MerlD, Mechanical and anticorrosion properties of nanosilica-filled epoxy-resin composite coatings. Appl Surf Sci. 2014;292:432–437. doi: 10.1016/j.apsusc.2013.11.155