Electrodeposition of NiFe films, on hydrogen-terminated n-Si (111)-H from acidic dilute sulphate solution, was studied by electrochemical measurements at room temperature in the presence and absence of saccharin. The electroplating process kinetics was investigated by voltammetric study and the effect of Fe2+ concentration on the deposit composition was studied as well with energy dispersive spectrometry analysis. The average composition of the Ni45Fe55 film was obtained for Fe2+ concentration in the range of [0.030–0.035] mol L−1 at a current density of −6 mA cm−2. Correlation between Fe2+ concentration in the NiFe deposit and electronic properties was examined by electrochemical impedance spectroscopy. Film roughness depends on Fe2+ concentration and a smoother deposit was obtained for the Ni45Fe55 film. Very low coercivity (less than 1.3 Oe) was measured in the Ni45Fe55 film with a nominal thickness of 640 nm. The very soft magnetic properties of the NiFe films provide information about the low level of inhomogeneities present in these films.
YooBY, HernandezSC, PardyK, Electrodeposition of FeCoNi thin films for magnetic-MEMS devices. Electrochim Acta. 2006;51:6346–6352. doi: 10.1016/j.electacta.2006.04.020
2.
PavithraGP, Chitharanjan HegdeA.Magnetic property and corrosion resistance of electrodeposited nanocrystalline iron-nickel alloys. Appl Surf Sci. 2012;258:6884–6890. doi: 10.1016/j.apsusc.2012.03.124
3.
TabakovicI, InturiV, ThurnJ, Properties of Fe1-xNix (0.1<x<0.9) and invar (x=0.64) alloys obtained by electrodeposition. Electrochim Acta. 2010;55:6749–6754. doi: 10.1016/j.electacta.2010.05.095
4.
KatalinN, AttilaC, KálmánV, Near-substrate composition depth profile of direct current-plated and pulse-plated Fe–Ni alloys. Electrochim Acta. 2013;103:179–187. doi: 10.1016/j.electacta.2013.04.063
5.
MyungNV, NobeK.Electrodeposited Iron group thin-film alloys. Structure-property relationships. J Electrochem Soc. 2001;148(3):C136–C144. doi: 10.1149/1.1345875
6.
YuYD, WeiGY, LouJW, Preparation of NiFe films by magnetic electroplating. Surf Eng. 2012;28(1):24–29. doi: 10.1179/1743294411Y.0000000063
7.
FazliS, BahrololoomME.Effect of plating time on electrodeposition of thick nanocrystalline permalloy foils. Trans IMF. 2016;94(2):92–98. doi: 10.1080/00202967.2015.1122918
8.
ErschingaK, IsoppobEA, TumelerocMA, Uniformity and homogeneity of FeXNi100−X nanowires electrodeposited in nanoporous alumina. J Phy Chem Solids. 2017;104:124–132. doi: 10.1016/j.jpcs.2017.01.008
9.
ZhangX, ZhangH, WuaT, Comparative study in fabrication and magnetic properties of FeNi alloy nanowires and nanotubes. J Magn Magn Mater. 2013;331:162–167. doi: 10.1016/j.jmmm.2012.11.033
10.
Brenner. Electrodeposition of alloys. New York
: Academic Press; 1963.
11.
AndricacosPC, RomankiwLT.Magnetically soft materials: Their properties and electrochemistry. In: GerischerH, TobiasCW, editors. Advances in electrochemical science and engineering V3. New York
: VCH Publishers; 1994.
12.
RobertsonN, HuHL.Ching Tsang, High performance write head using NiFe 45/55. IEEE Trans Magn. 1997;33(5):2818–2820. doi: 10.1109/20.617741
13.
Cooper EI, BonhoteC, HeidmannJ, Recent developments in high-moment electroplated materials for recording heads. J Res Develop. 2005;49:103–126.
14.
KojimaT, MizuguchiM, TakanashiK.Growth of L10–FeNi thin films on Cu(001) single crystal substrates using oxygen and gold surfactants. Thin Solid Films. 2016;603:348–352. doi: 10.1016/j.tsf.2016.02.040
15.
FriskA, LindgrenB, PappasSD, Resonant X-ray diffraction revealing chemical disorder in sputtered L10 FeNi on Si (0 0 1). J Phys Condens Matter. 2016;28:406002, 9 pp. doi: 10.1088/0953-8984/28/40/406002
16.
Li XH, YangZ.Effects of sputtering conditions on the structure and magnetic properties of Ni-Fe films. Mater Sci Eng B. 2004;106:41–45. doi: 10.1016/j.mseb.2003.07.003
17.
RookK, GuptaS, HieronymiR.Sputter deposition of 45% Ni - 55% Fe for high moment top pole applications. J Appl Phy. 2000;87:5843–5845. doi: 10.1063/1.372541
18.
OuirS, SamS, FortasG, FeNi alloys electroplated into porous (n-type) silicon. Phys Stat Sol. 2008;c:1–4.
19.
GaoLJ, MaP.Novogradecz KM, Norton PR, Characterization of permalloy thin films electrodeposited on Si(111) surfaces. J Appl Phys. 1997;81(11):7595–7599. doi: 10.1063/1.365305
20.
SpadaER, de OliveiraLS, da RochaAS, Thin films of FexNi1−x electroplated on silicon (100). J Magn Magn Mater. 2004;e891:272–276.
21.
ZarpellonJ, JurcaHF, KleinJJ, Electrodeposition de Fe thin films on Si(111) surfaces in the presence of sodium saccharin. Electrochim Acta. 2007;53:2002–2008. doi: 10.1016/j.electacta.2007.08.058
22.
HouX, LiuS, LiJ, Microstructure and Magnetic Properties of Electrodeposited Fe-Based Thin Films on Silicon Substrate Under Heat Treatment. Mater Manuf Process. 2015;0:1–5.
23.
O'DonnellT, WangN, KulkarniS, Electrodeposited anisotropic NiFe 45/55 thin films for high-frequency micro-inductor applications. J Magn Magn Mater. 2010;332:1690–1693. doi: 10.1016/j.jmmm.2009.01.038
24.
RoyS, ConnellA, LudwigM, Pulse reverse plating for integrated magnetic on Si. J Magn Magn Mater. 2005;290–291:1524–1527. doi: 10.1016/j.jmmm.2004.11.566
25.
HessamiS, TobiasCW.A mathematic model for Anomalous co-deposition of Nickel-Iron on a Rotating Disk Electrode. J Electrochem Soc. 1989;136:3611–3616. doi: 10.1149/1.2096519
26.
RashidiAM, AmadehA.The effect of saccharin addition and bath temperature on the grain size of nanocrystalline nickel coatings. Surf Coat Technol. 2009;204:353–358. doi: 10.1016/j.surfcoat.2009.07.036
27.
BrankovicSR.Saccharin effect on properties of 2.4 T CoFe Films. Electrochim Acta. 2012;84:139–144. doi: 10.1016/j.electacta.2012.07.061
VaesJ, FransaerJ, CelisJP.Cathodic inhibition effects during NiFe and ZnNi alloy deposition. J Electrochem Soc. 2002;149(11):C567–C572. doi: 10.1149/1.1511189
30.
NakanoH, MatsunoM, OueS, Mechanism of Anomalous Type Electrodeposition of Fe-Ni Alloys from Sulfate Solutions. Mater Trans. 2004;45(11):3130–3135. doi: 10.2320/matertrans.45.3130
31.
KernerZ, PajkossyT.Impedance of rough capacitive electrodes: The role of surface disorder. J Electroanal Chem. 1998;448:139–142. doi: 10.1016/S0022-0728(98)00025-4
32.
Córdoba-TorresP, MesquitaTJ, DevosO, On the intrinsic coupling between constant-phase element parameters α and Q in electrochemical impedance spectroscopy. Electrochim Acta. 2012;72:172–178. doi: 10.1016/j.electacta.2012.04.020
33.
JurczakowskiR, HitzC, LasiaA.Impedance of porous Au based electrodes. J Electroanal Chem. 2004;572:355–366. doi: 10.1016/j.jelechem.2004.01.008
34.
Van der ZaagPJ, JohnsonMT, RuigrokJJM, The grain boundary influence on the coercivity of polycrystalline MnZn-ferrites. J Magn Magn Mater. 1994;129:L137–L140. doi: 10.1016/0304-8853(94)90103-1
35.
KocharH, AlperM, KuruH, Magnetic anisotropy and its thickness dependence for NiFe alloy films electrodeposited on polycrystalline Cu substrates. J Magn Magn Mater. 2006;304:e736–e738. doi: 10.1016/j.jmmm.2006.02.207