Quantitative X-Ray analysis was used to quantify the phase content generated by the High Velocity Oxygen Fuel (HVOF) process following the decarburisation of WC–Co coatings. Rietveld analysis was used to quantify the different phases present. Particular attention has been made to identifying the sequence of formation of the different species, namely: during flight of the powders towards the substrate and/or during the solidification and cooling step on the substrate. The results show that decarburisation is influenced by the thermal history of the particles in flight. In particular, more W2C and W are generated with increasing spray distance indicating an increase WC decarburisation. During the coating building-up, new nanosized compounds (W3Co3C and W6Co6C) were generated. These compounds, at the reverse of W2C and W phases, decrease with the stand-off distance. Correlations are established between the mechanical properties (microhardness and crack propagation resistance) and the content of the phases determined from the Rietveld analysis.
KumarasamyM, NatarajanS.Selection and characterisation of HVOF cermet coatings for volutes of high capacity pumps of open cast lignite mines. Surf Eng. 2016;32(3):229–237. doi: 10.1179/1743294415Y.0000000015
2.
BolelliG.Replacement of hard chromium plating by thermal spraying–problems, solutions and possible future approaches. Surf Eng. 2009;25(4):263–269. doi: 10.1179/174329409X373729
3.
XieY, XiaohanP, SongboW.Investigation of erosion resistance property of WC-Co coatings. Int J Surf Sci Eng. 2016;10(4):365–374. doi: 10.1504/IJSURFSE.2016.077536
4.
GengZ, DuanDL, LiuY, The effect of oxidation at elevated temperature on tribological behavior of WC-Co HVOF spraying coatings. Tribol.2013;33(4):329–336.
5.
DentAH, DePaloS, SampathS.Examination of the wear properties of HVOF sprayed nanostructured and conventional WC-Co cermets with different binder phase contents. J Thermal Spray Technol. 2002;11(4):551–558. doi: 10.1361/105996302770348691
6.
La Barbera-SosaJG, SantanaYY, CaroJ, Mechanical properties of WC coatings evaluated using instrumented indentation technique. Surf Eng. 2014;30(7):499–510. doi: 10.1179/1743294414Y.0000000261
7.
HazraS, SabiruddinK, BandyopadhyayPP.Plasma and HVOF sprayed WC–Co coatings as hard chrome replacement solution. Surf Eng. 2012;28(1):37–43. doi: 10.1179/1743294410Y.0000000009
8.
MasukuZH, OlubambiPA, PotgieterJH, Tribological and corrosion behavior of HVOF sprayed WC-Co-based composite coatings in simulated mine water environments. Tribol Trans. 2015;58:337–348. doi: 10.1080/10402004.2014.971994
9.
ÖzbekYY, CanikogluN, IpekM.The mechanical properties and wear resistance of HVOF sprayed WC–Co coatings. Acta Phys Polonica A. 2016;129(4):600–603. doi: 10.12693/APhysPolA.129.600
10.
SpadloS, DepczynskiW, MlynarczykP.Selected properties of high velocity oxy liquid fuel (HVOLF)-sprayed nanocrystalline WC-Co infralloy tms7412 coatings modified by high energy electric pulse. Metalurgija. 2017;56(3–4):412–414.
11.
BouarichaS, LegouxJG.CladdingWC-Co based materials to protect them from decarburization caused by the heat of the thermal spray gun. Surf and Coat Technol. 2017;309:355–362. doi: 10.1016/j.surfcoat.2016.09.076
12.
De Villiers LovelockHL, RichterPW, BensonJM, Study of HP/HVOF deposited WC-Co coatings. J Therm Spray Technol. 1998;7(1):97–107. doi: 10.1007/s11666-006-5010-x
13.
LiCJ, OhmoriA, HaradaY.Effect of powder structure on the structure of thermally sprayed WC-Co coatings. J Mater Sci. 1996;31(3):785–794. doi: 10.1007/BF00367900
14.
AfzalM, AjmalM, KhanAN.Wear behavior of WC-12%Co coatings produced by air plasma spraying at different standoff distances. Tribol Trans2014;57(1):94–103. doi: 10.1080/10402004.2013.850763
15.
SantanaYY, La Barbera-SosaJG, BencomoA, Influence of mechanical properties of tungsten carbide–cobalt thermal spray coatings on their solid particle erosion behaviour. Surf Eng. 2012;28(4):237–243. doi: 10.1179/1743294411Y.0000000016
16.
VerdonC, KarimiA, MartinJL.A study of high velocity oxy-fuel thermally sprayed tungsten carbide based coatings. Part 1: microstructures. Mater Sci Eng. 1998;A246(1–2):11–24. doi: 10.1016/S0921-5093(97)00759-4
17.
AnstisGR, ChantikulP, LawnBR, A critical evaluation of indentation techniques for measuring fracture toughness: I. Direct crack measurements. J Am Ceram Soc. 1981;64(9):1073–1082. doi: 10.1111/j.1151-2916.1981.tb10320.x
YoungRA.The Rietveld method. International union of crystallography. oxford, England
: Oxford Science Publications; 1993.
20.
MarpleBR, LimaRS.Thermal spray 2003: advancing the science & applying the technology. MoreauC and MarpleBR, editors, Materials Park (OH
): SM International; 2003; pp.273.
21.
BouarichaS, MarpleB R.Phase structure-mechanical property relationship in HVOF-Sprayed WC-12Co coatings. Proceedings of the International Thermal Spray Conference 3-87155-792-7, Osaka Japan (2004). Advances in Technology and Application, ASM International, Materials Park, OH. (2004): 516–522.
22.
ZhanQ, YuL, YeF, Quantitative evaluation of the decarburization and microstructure evolution of WC–Co during plasma spraying. Surf Coat Technol. 2012;206(19-20):4068–4074. doi: 10.1016/j.surfcoat.2012.03.091
23.
YuanJ, ZhanQ, HuangJ, Decarburization mechanisms of WC-Co during thermal spraying: insights from controlled carbon loss and microstructure characterization. Mater Chem Phys. 2013;142:165–171. doi: 10.1016/j.matchemphys.2013.06.052
ThieleS, SempfK, Jaenicke-RoesslerK, Thermo-physical and microstructural studies on thermally sprayed tungsten carbide-cobalt coatings. J Therm Spray Technol. 2011;20(1-2):358–365. doi: 10.1007/s11666-010-9558-0
26.
WangQ, ChenZH, DingZX.Performance of abrasive wear of WC–12Co coatings sprayed by HVOF. Tribol Int. 2009;42(7):1046–1051. doi: 10.1016/j.triboint.2009.02.011
27.
PicasJA, PunsetM, Teresa BaileM, Tribological evaluation of HVOF thermal-spray coatings as a hard chrome replacement. Surf Interface Anal.2011;43:1346–1353. doi: 10.1002/sia.3721
28.
GuilemanyJM, De PacoM, NuttingJ, Characterization of the W2C phase formed during the high velocity oxygen fuel spraying of a WC + 12 Pct Co powder. Metall Mater Trans A. 1999;30(8):1913–1921. doi: 10.1007/s11661-999-0002-3
29.
Di GirolamoG, MarraF, PilloniL, Microstructure and wear behavior of plasma-sprayed nanostructured WC–Co coatings. Int J Appl Ceram Technol. 2013;10(1):60–71. doi: 10.1111/j.1744-7402.2011.02734.x
30.
WatanabeM, OwadaA, KurodaS, Effect of WC size on interface fracture toughness of WC–Co HVOF sprayed coatings. Surf Coat Technol. 2006;201(3-4):619–627. doi: 10.1016/j.surfcoat.2005.12.019
31.
ShawL, LuoH, ZhongY.WC-18 wt.% Co with simultaneous improvements in hardness and toughness derived from nanocrystalline powder. Mat Sci Eng A. 2012;537:39–48. doi: 10.1016/j.msea.2012.01.005
32.
SobolevVV, GuilemanyJM.Oxidation processes can occur during both the in-flight motion of the powder particles and exposure of the solidifying splats to the surrounding oxygen rich atmosphere. Mater Lett. 1998;37(4):231–235. doi: 10.1016/S0167-577X(98)00097-4