A Zr–Y alloyed layer was prepared onto the surface of γ-TiAl using double-glow plasma surface alloying technique (DG technique). The results showed that the Zr–Y alloyed layer was comprised of deposited sub-layer and diffused sub-layer, with a total layer thickness of about 20 μm. The nano-indentation test result showed that the nano-hardness of Zr–Y alloyed layer was 2.35 times that of γ-TiAl. The scratch test was carried to evaluate the adhesion strength of Zr–Y alloyed layer. The tribological behaviours were investigated both at ambient temperature and 500°C. Under dry sliding condition, the friction coefficient of the Zr–Y alloyed layer was lower than that of the γ-TiAl. The specific wear rate of γ-TiAl in the presence of Zr–Y alloyed layer was approximately one fifth that in the absence of the alloyed layer. The excellent wear resistance of Zr–Y alloyed layer could be attributed to the high hardness or load-carrying ability.
HabelU, HeutlingF, KunzeC, Forged intermetallic γ-TiAl based alloy low pressure turbine blade in the geared turbofan. Hoboken (NJ)
: John Wiley & Sons, Inc; 2016.
4.
SpiessP, BartosinskiM, StoyanovT, A closed-loop recycling technology for γ-TiAl from precision cast low pressure turbine blades. Chem-Ing-Tech. 2015;87(11):1580–1588. doi: 10.1002/cite.201500063
5.
SudarshanTS, BhatDG.Surface modification technologies. 135-136(132). New York
: M. Dekker; 1989.
6.
QinYK, XiongDS, LiJL, Compositions and tribological properties of PEO coatings on Ti6Al4V alloy. Surf Eng. 2016:1–7. doi:10.1179/1743294414Y.0000000412.
7.
MaliutinaIN, Si-MohandH, PioletR, Mechanical and tribological properties of γ-TiAl-based coatings produced by the laser cladding technology. Appl Mech Mater. 2015;788:194–198. doi: 10.4028/www.scientific.net/AMM.788.194
8.
HeN, LiH, JiL, High temperature tribological properties of TiAlSiN coatings produced by hybrid PVD technology. Tribol Int. 2016;98:133–143. doi: 10.1016/j.triboint.2016.02.034
9.
ChenXH, ZhangPZ, WeiDB, Surface modification of pure titanium by plasma tantalumising. Surf Eng. 2013;29(3):228–233. doi: 10.1179/1743294412Y.0000000107
10.
DuanBZ, ZhangPZ, WeiXF, Effects of elements W and C on microstructure and wear property of γ-TiAl surface alloying layer. Surf Eng. 2014;31(12):942–948. doi: 10.1179/1743294414Y.0000000386
11.
HuangJ, ZhangPZ, WuHY, Investigation of W–Mo alloyed layer synthesised by double glow plasma surface metallurgy. Surf Eng. 2013;27(2):113–117.
12.
WeiD, ZhangP, YaoZ, Double glow plasma chromizing of Ti6Al4V alloys: impact of working time, substrate–target distance, argon pressure and surface temperature of substrate. Vacuum. 2015;121:81–87. doi: 10.1016/j.vacuum.2015.08.001
13.
WuH, LiY, TangX, Nano-mechanical characterization of plasma surface tungstenized layer by depth-sensing nano-indentation measurement. Appl Surf Sci. 2015;324:160–167. doi: 10.1016/j.apsusc.2014.10.085
14.
JiangAL, ZhangPZ, HuangJ.Microstructure and tribological properties of Zr permeating layer on TC11 titanium alloy surface. Mater Mech Eng. 2011;35(9):14–17.
15.
WuY, HwangSK, NamSW, The effect of yttrium addition on the oxidation resistance of EPM TiAl-based intermetallics. Scr Mater. 2003;48(12):1655–1660. doi: 10.1016/S1359-6462(03)00134-9
16.
WuY, HagiharaK, UmakoshiY.Influence of Y-addition on the oxidation behavior of Al-rich γ-TiAl alloys. Intermetallics. 2004;12(5):519–532. doi: 10.1016/j.intermet.2004.01.008
17.
BaeK, LeeS, DongYJ, High-performance protonic ceramic fuel cells with thin-film yttrium-doped barium cerate–zirconate electrolytes on compositionally gradient anodes. ACS Appl Mater Inter. 2016;8(14):9097–9103. doi: 10.1021/acsami.6b00512
18.
XueH, YangG, LiD, Effects of yttrium addition on microstructure and mechanical properties of AZ80-2Sn magnesium alloys. High Temp Mater Process. 2015;34(1):86–92.
19.
LaskaN, BraunR.Oxidation and fatigue behaviour of gamma titanium aluminides coated with yttrium or zirconium containing intermetallic Ti–Al–Cr layers and thermal barrier coating. Mater High Temp. 2015;32(1–2):221–229. doi: 10.1179/0960340914Z.000000000104
20.
HuZ.Characterization of materials’ elasticity and yield strength through micro-/nano-indentation testing with a cylindrical flat-tip indenter. Int J Mater Res. 2015;30(4):578–591. doi: 10.1557/jmr.2015.4
21.
DongS, BeakeBD, ParkinsonR, Determination of hardness and Young's modulus of brush plated Nano-ALO/NI composite coating by nanoindentation testing. Surf Eng. 2003;19(3):195–199. doi: 10.1179/026708403225006168
22.
ZhaX, WangN, JiangF, Performance evaluation of PVD coatings due to sequential indentation tests. Surf Eng. 2016:1–8. doi:10.1080/02670844.2016.1161947.
23.
QiuZK, ZhangPZ, WeiDB, Mechanical and electrochemical properties of Zr and Zr-Er alloyed layers deposited on titanium alloy (TC11). Surf Coat Technol. 2015;280:301–307. doi: 10.1016/j.surfcoat.2015.09.031
24.
LeylandA, MatthewsA.On the significance of the H/E ratio in wear control: a nanocomposite coating approach to optimised tribological behaviour. Wear. 2000;246(1–2):1–11. doi: 10.1016/S0043-1648(00)00488-9
25.
MehrotraK, OliverJB, LambropoulosJC.Nano-indentation of single-layer optical oxide thin films grown by electron-beam deposition. Appl Opt. 2015;54(9):2435–2440. doi: 10.1364/AO.54.002435
26.
RenJ, LiuXB, LuXL, Microstructure and tribological properties of self-lubricating antiwear composite coating on Ti6Al4V alloy. Surf Eng. 2016. doi:10.1179/1743294415Y.0000000054.
27.
ThirugnanasambanthamKG, NatarajanS.Degradation mechanism for high temperature erosion in surface modified IN718 superalloy. Surf Eng. 2015;31(1):24–28. doi: 10.1179/1743294414Y.0000000377
28.
QiuZK, ZhangPZ, WeiDB, Tribological behavior of CrCoNiAlTiY coating synthesized by double-glow plasma surface alloying technique. Tribol Int. 2015;92:512–518. doi: 10.1016/j.triboint.2015.07.038
29.
SankaranR, RajamaniD, NatarajanS, Sliding wear behaviour and its mechanisms of carbonitrided AISI 8620 steel at 100°C under unlubricated conditions. Surf Eng. 2016. doi:10.1179/1743294415Y.0000000090.