An electrolytic process was utilised to fabricate NiCoCrAlY coatings, involving deposition of a composite coating consisting of the (Ni,Co) matrix and CrAlY particles, followed by a diffusion heat treatment to convert the composite coating to the desired NiCoCrAlY microstructure. This study focused on the effects of the post-deposition heat-treating conditions (temperature and atmosphere) on the final coating microstructure and composition. The (Ni,Co)–CrAlY composite coatings were heat-treated for 2 h at 1000, 1100 and 1200°C in vacuum and Ar, respectively. Phase constituents and concentrations of the major elements in the coating after heat treatment were examined. Vacuum heat treatment at temperatures ≥1100°C resulted in a significant decrease in Cr content at the coating surface due to Cr evaporation. Heat treatment at 1200°C also caused outward diffusion of Ti from the substrate alloy to the coating layer.
WrightI. G. and GibbonsT. B., ‘Recent developments in gas turbine materials and technology and their implications for syngas firing’, Int. J. Hydrogen Energy, 2010,
32, 3610–3621.
2.
PintB. A., GarnerG. W., LoweT. M., HaynesJ. A. and ZhangY., ‘Effect of increased water vapor levels on TBC lifetime with Pt-containing bond coatings’, Surf. Coat. Technol., 2011,
206, 1566–1570.
3.
GowardG. W., ‘Progress in coatings for gas turbine airfoils’, Surf. Coat. Technol., 1998,
108–109, 73–79. doi: 10.1016/S0257-8972(98)00667-7
4.
PadtureN. P., GellM. and JordanE. H., ‘Thermal barrier coatings for gas-turbine engine applications’, Science, 2002,
296, 280–284.
5.
MeierS. M., GuptaD. K. and ShefflerK. D., ‘Ceramic thermal barrier coatings for commercial gas turbine engines’, JOM, 1991,
43, 50–53.
6.
TaheriM., ValefiZ. and Zangeneh-MadarK., ‘Influence of HVOF process parameters on microstructure and bond strength of NiCrAlY coatings’, Surf. Eng., 2012,
28, 266–272.
7.
MévrelR., ‘State of the art on high-temperature corrosion-resistant coatings’, Mater. Sci. Eng., 1989,
120–121, 13–24.
8.
FosterJ., CameronB. P. and CarewJ. A., ‘The production of multi-component alloy coatings by particle codeposition’, Trans. Inst. Met. Finish, 1985,
63, 115–119.
9.
HoneyF. J., KedwardE. C. and WrideV., ‘The development of electrodeposits for high-temeprature oxidation/corrosion resistance’, J. Vac. Sci. Technol., 1986,
4, 2593–2597.
10.
LuX., ZhuR. and HeY., ‘Electrophoretic deposition of MCrAlY overlay-type coatings’, Oxid. Met., 1995,
43, 353–362.
11.
BacosM.-P., GirardB., JossoP. and RioC., ‘MCrAlY coating developed via a new electroless-like route: Influence of deposition parameters’, Surf. Coat. Technol., 2003,
162, 248–260.
12.
MercierS., GiovannetiI., JossoP. and BacosM.-P., ‘Analysis of the co-deposition of CrAlYTa particles with nickel by an electrolytic-electroless route: The influence of solution and hydrodynamic parameters’, Surf. Coat. Technol., 2006,
201, 120–128.
13.
LowC. T. J., WillsR. G. A. and WalshF. C., ‘Electrodeposition of composite coatings containing nanoparticles in a metal deposit’, Surf. Coat. Technol., 2006,
201, 371–383.
14.
MokabberT., RastegariS. and RazavizadehH., ‘Effect of electroplating parameters on properties of Zn–nano-TiO2 composite coatings’, Surf. Eng., 2013,
29, 41–45.
15.
WalshF. C. and Ponce de LeonC., ‘A review of the electrodeposition of metal matrix composite coatings by inclusion of particles in a metal layer: an established and diversifying technology’, Trans. Inst. Met. Finish, 2014,
92, 83–98.
16.
ArunaS. T. and SrinivasG., ‘Wear and corrosion resistant properties of electrodeposited Ni composite coating containing Al2O3–TiO2 composite powder’, Surf. Eng., 2015,
31, 708–713.
BatesB. L., ZhangL. Z. and ZhangY., ‘Electrodeposition of Ni matrix composite coatings with embedded CrAlY particles’, Surf. Eng., 2015,
31, 202–208.
19.
BatesB. L., WitmanJ. C. and ZhangY., ‘Electrolytic codeposition of Ni-CrAlY composite coatings using different deposition configurations’, Mater. Manuf. Process, 2016, 31, 1232–1237.
20.
SusanD. F., MisiolekW. Z. and MarderA. R., ‘Reaction synthesis of Ni-Al–based particle composite coatings’, Metall. Mater. Trans. A, 2001,
32A, 379–390.
21.
NijdamT. J., JeurgensL. P. H., ChenJ. H. and SloofW. G., ‘On the microstructure of the initial oxide grown by controlled annealing and oxidation on a NiCoCrAlY bond coating’, Oxid. Met., 2005,
64, 355–377.
22.
KellerI., NaumenkoD., QuadakkersW. J., VaßenR. and SingheiserL., ‘Influence of vacuum heat treatment parameters on the surface composition of MCrAlY coatings’, Surf. Coat. Technol., 2013,
215, 24–29.
23.
WoodJ. H. and GoldmanE. H.: ‘Protective Coatings’ in ‘Superalloys II’, (ed. SimsC. T..), 359–384; 1987, New York, NY, John Wiley & Sons.
24.
HadjiapostolidouD. and ShollockB. A. in ‘Superalloys 2008’, (ed. ReedR. C..), 733–739; 2008, Warrendale, PA, TMS (The Minerals, Metals & Materials Society).
25.
Vande PutA., LafontM. C., OquabD., RaffaitinA. and MonceauD., ‘Effect of modification by Pt and manufacturing processes on the microstructure of two NiCoCrAlYTa bond coatings intended for thermal barrier system applications’, Surf. Coat. Technol., 2010,
205, 717–727.
26.
Vande PutA., OquabD., PéréE., RaffaitinA. and MonceauD., ‘Beneficial effect of Pt and of pre-oxidation on the oxidation behaviour of an NiCoCrAlYTa bond-coating for thermal barrier coating systems’, Oxid. Met., 2011,
75, 247–279.