In the current study, the influence of welding speed (500, 700 and 800 mm/min) and post-weld heat treatment (PWHT) on microstructure and mechanical properties of electron beam welded Ti-15V-3Al-3Cr-3Sn was systematically studied. The welds at 800 mm/min welding speed showed higher ultimate tensile strength (UTS) (751 MPa), and hardness (245 HV) compared to welds prepared with 500 mm/min welding speed (UTS 670 MPa; hardness 235 HV). The higher strength at 800 mm/min welding can be attributed to the lower columnar width of β grains and the formation of equiaxed grains at the weld root and centre. A significant increase in UTS and hardness values was observed in samples subjected to the post-weld heat treatment (PWHT) for all the weld speeds.
KarJRoySKRoyGG.Influence of beam oscillation in electron beam welding of Ti-6AL-4V. Int J Adv Manuf Technol. 2018;94:4531–4541. DOI:10.1007/s00170-017-1169-1
2.
EliezerDBoellinghausT.Hydrogen behavior in GTA welded Ti-6Al-4V and beta-21S aerospace applicative titanium alloys. Mater Sci Forum. 2007;549:1413–1420. DOI:10.4028/www.scientific.net/MSF.546-549.1413
3.
HsiehCTShiueRKHuangRMaterials science & engineering A The effect of post-weld heat treatment on the microstructure and notched tensile fracture of Ti – 15V – 3Cr – 3Al – 3Sn to Ti – 6Al – 4V dissimilar laser welds. Mater Sci Eng A. 2016;653:139–146. DOI:10.1016/j.msea.2015.12.013
4.
BanothRSarkarRBhattacharjeeAEffect of boron and carbon addition on microstructure and mechanical properties of metastable beta titanium alloys. J Mater. 2015;67:50–63. DOI:10.1016/j.matdes.2014.11.004
5.
RosenbergHW.Ti-15-3 : a new cold-formable sheet titanium alloy. JOM. 1983;35:30–34. DOI:10.1007/BF03339165
6.
SanthoshRGeethaMSaxenaVKEffect of duplex aging on microstructure and mechanical behavior of beta titanium alloy Ti – 15V – 3Cr – 3Al – 3Sn under unidirectional and cyclic loading conditions. Int J Fatigue. 2015;73:88–97. DOI:10.1016/j.ijfatigue.2014.12.005
7.
BabuNKRamanSGSMurthyCVSEffect of beam oscillation on fatigue life of Ti-6Al-4V electron beam weldments. Mater Sci Eng A. 2007;471:113–119. DOI:10.1016/j.msea.2007.03.040
8.
CottrellCLM.Electron beam welding – a critical review. Mater Des. 1985;6:285–291. DOI:10.1016/0261-3069(85)90009-3
9.
LinHCWangLM.Improved mechanical properties of Ti – 15V – 3Cr – 3Sn – 3Al alloy by electron beam welding process plus heat treatments and its microstructure evolution. Mater Chem Phys. 2011;126:891–897. DOI:10.1016/j.matchemphys.2010.12.019
10.
PasangTSánchez AmayaJMTaoYComparison of Ti-5Al-5V-5Mo-3Cr welds performed by laser beam, electron beam and gas tungsten arc welding. Procedia Eng. 2013;63:397–404. DOI:10.1016/j.proeng.2013.08.202
11.
SabolJCPasangTMisiolekWZJournal of materials processing technology localized tensile strain distribution and metallurgy of electron beam welded Ti – 5Al – 5V – 5Mo – 3Cr titanium alloys. J Mater Process Tech. 2012;212:2380–2385. DOI:10.1016/j.jmatprotec.2012.06.023
12.
TingWBing-gangZGuo-qingC.Electron beam welding of Ti-15-3 titanium alloy to 304 stainless steel with copper interlayer sheet. Trans Nonferrous Met Soc China. 2010;20:1829–1834. DOI:10.1016/S1003-6326(09)60381-2
13.
BalachandarKSarmaVSPantB.Microstructure and mechanical properties of gas-tungsten- arc – welded Ti-15-3 beta titanium alloy. Metall Mater Trans. 2009;40:2685–2693. DOI:10.1007/s11661-009-9952-8
14.
BeckerDWBaeslackWAIII.Property-microstructure relationships in metastable-beta titanium alloy weldments. Weld J. 1980;124:85–92.
15.
SanthoshRGeethaMSaxenaVKStudies on single and duplex aging of metastable beta titanium alloy Ti-15V-3Cr-3Al-3Sn. J Alloys Compd. 2014;605:222–229. DOI:10.1016/j.jallcom.2014.03.183
16.
YumakNAslantaşK.Effect of heat treatment procedure on mechanical properties of Ti-15V-3Al-3Sn-3Cr metastable β titanium alloy. J Mater Eng Perform. 2021;30:1066–1074. DOI:10.1007/s11665-020-05445-x
17.
YumakNAslantaşKÇetkinA.Cryogenic and aging treatment effects on the mechanical properties of Ti-15V3Al-3Cr-3Sn titanium alloy. J Test Eval. 2020;49; DOI:10.1520/JTE20200078
18.
KurodaTMatsudaFIwagiI.Effects of two-step ageing and thermomechanical treatments on age-hardening properties of welded β titanium alloy effects of two-step ageing and thermomechanical treatments on age-hardening properties of welded β titanium alloy. Weld Int. 2016;8(1):9–15. DOI:10.1080/09507119409548536
19.
LutAKumarMBabuNKGrain refinement of Ti-15V-3Cr-3Sn-3Al metastable b titanium alloy welds using boron-modified fillers. J Alloys Compd. 2018;749:320–328. DOI:10.1016/j.jallcom.2018.03.286
20.
BerminghamMJStJohnDHKrynenJPromoting the columnar to equiaxed transition and grain refinement of titanium alloys during additive manufacturing. Acta Mater. 2019;168:261–274. DOI:10.1016/j.actamat.2019.02.020
21.
SundaresanSJanaki RamGDMadhusudhan ReddyG.Microstructural refinement of weld fusion zones in α-β titanium alloys using pulsed current welding. Mater Sci Eng A. 1999;262:88–100. DOI:10.1016/s0921-5093(98)01010-7
22.
BabuNKRamanSGSMurthyCVSInfluence of beam oscillation patterns on the structure and mechanical properties of Ti-6Al-4V electron beam weldments. Sci Technol Weld Join. 2005;10:583–590. DOI:10.1179/174329305X57473
23.
KouSLeY.Welding parameters and the grain structure of weld metal – a thermodynamic consideration. Metall Trans A Phys Metall Mater Sci. 1988;19A:1075–1082. DOI:10.1007/bf02628392
24.
KishoreBNAshfaqM.Influence of welding speed on microstructure and mechanical properties of AZ31 magnesium alloy laser weldments. Prakt Metallogr Metallogr. 2010;47:426–442. DOI:10.3139/147.110097
25.
MishraSDebRoyT.Measurements and Monte Carlo simulation of grain growth in the heat-affected zone of Ti-6Al-4V welds. Acta Mater. 2004;52:1183–1192. DOI:10.1016/j.actamat.2003.11.003
PasangTTaoYAziziMWelding of titanium alloys. MATEC Web Conf. 2017;123:1–8. DOI:10.1051/matecconf/201712300001
28.
SanthoshRGeethaMNageswara RaoM.Recent developments in heat treatment of beta titanium alloys for aerospace applications. Trans Indian Inst Met. 2017;70:1681–1688. DOI:10.1007/s12666-016-0985-6
29.
WangSHWeiMD.Tensile properties of gas tungsten arc weldments in commercially pure titanium, Ti-6Al-4V and Ti-15V-3Al-3Sn-3Cr alloys at different strain rates. Sci Technol Weld Join. 2004;9:415–422. DOI:10.1179/136217104225021599