To clarify the effect of post-heat treatment on the microstructure and mechanical properties of the coarse-grained heat-affected zone (CGHAZ) for EH47 steel, simulated CGHAZ specimens were subjected to post-heat treatment at 250°C for 1.0 h. The results showed that the microstructure of CGHAZ was composed of granular bainite (GB) and lath bainite (LB), and a large number of iron-carbon particles (∼81 nm) were precipitated after post-heat treatment. The relationship between dislocations, low-angle grain boundaries and iron-carbon particles was revealed by KAM values. The iron-carbon particles hindered the movement of sub-grain boundaries and dislocations, thereby increased the yield strength (∼120 MPa). The precipitation of iron-carbon particles caused the cracking of bainite ferrite and reducing the fracture toughness of CGHAZ.
TaylorJMehmanparastAKulkaRCompact crack arrest testing and analysis of EH47 shipbuilding steel. Theor Appl Fract Mech. 2021;114:103004. doi:10.1016/j.tafmec.2021.103004.
2.
SumiYYajimaHToyosadaMFracture control of extremely thick welded steel plates applied to the deck structure of large container ships. J Mar Sci Technol. 2013;18:497–514. doi:10.1007/s00773-013-0222-5.
3.
HandaTSuzukiSKijiNEffect of unwelded length on behaviour of brittle crack arrest in T-joint structure. Weld Int. 2009;23:640–647. doi:10.1080/09507110902842810.
4.
WuJYWangBWangBXToughness and ductility improvement of heavy EH47 plate with grain refinement through inter-pass cooling. Mater Sci Eng A. 2018;733:117–127. doi:10.1016/j.msea.2018.07.001.
5.
ZhouHZhangQYYiBHardness prediction based on microstructure evolution and residual stress evaluation during high tensile thick plate butt welding. Int J Nav Arch Ocean. 2020;12:146–156. doi:10.1016/j.ijnaoe.2019.09.004.
6.
LiCWWangYHanTMicrostructure and toughness of coarse grain heat-affected zone of domestic X70 pipeline steel during in-service welding. J Mater Sci. 2011;46:727–733. doi:10.1007/s10853-010-4803-y.
7.
XieHDuLXHuJEffect of thermo-mechanical cycling on the microstructure and toughness in the weld CGHAZ of a novel high strength low carbon steel. Mater Sci Eng A. 2015;639:482–488. doi:10.1016/j.msea.2015.05.033.
8.
LanLYQiuCLZhaoDWMicrostructural characteristics and toughness of the simulated coarse grained heat affected zone of high strength low carbon bainitic steel. Mater Sci Eng A. 2011;529:192–200. doi:10.1016/j.msea.2011.09.017.
9.
DiXTongMLiCMicrostructural evolution and its influence on toughness in simulated inter-critical heat affected zone of large thickness bainitic steel. Mater Sci Eng A. 2019;743:67–76. doi:10.1016/j.msea.2018.11.070.
10.
GuoWCaiYWangBEffect of microstructure synergism on cryogenic toughness for CGHAZ of low-carbon martensitic steel containing nickel. Mater Sci Eng A. 2021;830:142240. doi:10.1016/j.msea.2021.142240.
11.
YangXDiXLiuXEffects of heat input on microstructure and fracture toughness of simulated coarse-grained heat affected zone for HSLA steels. Mater Char. 2019;155:109818. doi:10.1016/j.matchar.2019.109818.
12.
DengJYangPDongQResearch on CTOD for low-cycle fatigue analysis of central-through cracked plates considering accumulative plastic strain. Eng Fract Mech. 2016;154:128–139. doi:10.1016/j.engfracmech.2015.11.021.
13.
LuoXChenXWangTEffect of morphologies of martensite-austenite constituents on impact toughness in intercritically reheated coarse-grained heat-affected zone of HSLA steel. Mater Sci Eng A. 2018;710:192–199. doi:10.1016/j.msea.2017.10.079.
14.
YueX.Investigation on heat-affected zone hydrogen-induced cracking of high-strength naval steels using the Granjon implant test. Weld World. 2014;59:77–89. doi:10.1007/s40194-014-0181-4.
15.
SchauppTErnstWSpindlerHHydrogen-assisted cracking of GMA welded 960 MPa grade high-strength steels. Int J Hydrog Energy. 2020;45:20080–20093. doi:10.1016/j.ijhydene.2020.05.077.
16.
KangYKimMKimGCharacteristics of susceptible microstructure for hydrogen-induced cracking in the coarse-grained heat-affected zone of carbon steel. Metall Mater Trans A. 2020;51:2143–2153. doi:10.1007/s11661-020-05671-x.
17.
ParkCKangNLiuS.Effect of grain size on the resistance to hydrogen embrittlement of API 2W Grade 60 steels using in situ slow-strain-rate testing. Corros Sci. 2017;128:33–41. doi:10.1016/j.corsci.2017.08.032.
18.
MenteTBoellinghausTSchmitz-NiederauM.Heat treatment effects on the reduction of hydrogen in multi-layer high-strength weld joints. Weld World. 2012;56:26–36. doi:10.1007/BF03321362.
19.
SchauppTRhodeMYahyaouiHInfluence of heat control on hydrogen distribution in high-strength multi-layer welds with narrow groove. Weld World. 2018;63:607–616. doi:10.1007/s40194-018-00682-0.
20.
AbeMNakataniMNamatameNInfluence of dehydrogenation heat treatment on hydrogen distribution in multi-layer welds of Cr–Mo–V steel. Weld World. 2012;56:114–123. doi:10.1007/BF03321355.
21.
Det Norske Veritas (DNVGL). Fabrication and testing of offshore structures. Oslo: DNVGL; 2020; DNVGL-OS-C401:2020.
22.
Det Norske Veritas (DNVGL). Design of offshore steel structures, general-LRFD method. Oslo: DNVGL; 2015; DNVGL-OS-C101:2015.
23.
WangYHuSLiYImproved hydrogen embrittlement resistance after quenching–tempering treatment for a Cr-Mo-V high strength steel. Int J Hydrogen Energy. 2019;44:29017–29026. doi:10.1016/j.ijhydene.2019.09.142.
24.
Det Norske Veritas (DNVGL). Metallic materials. Oslo: DNVGL; 2017; DNVGL-OS-B101:2017.
25.
Standardization Administration Of The People's Republic Of China (SAC). Metallic materials-tensile testing – Part 1: method of test at room temperature. Beijing: SAC; 2021; GB/T 228.1:2021.
26.
British Standard Institution (BSI). Fracture mechanics toughness tests – Part 2. method for determination of KIc, critical COD and critical J values of welds in metallic materials. London: (BSI); 1997; BS 7448: Part 2:1997.
27.
Standardization Administration Of The People's Republic Of China (SAC). Determination of estimating the average grain size of metal. Beijing: SAC; 2017; GB/T 6394:2017.
28.
TongMDiXLiCToughening mechanism of inter-critical heat-affected zone in a 690 MPa grade rack plate steel. Mater Char. 2018;144:631–640. doi:10.1016/j.matchar.2018.08.021.
29.
LiangJWShenYFMisraRDKHigh strength-superplasticity combination of ultrafine-grained ferritic steel: The significant role of nanoscale carbides. J Mater Science Technol. 2021;83:131–144. doi:10.1016/j.jmst.2020.11.078.
30.
KitaharaHUejiRTsujiNCrystallographic features of lath martensite in low-carbon steel. Acta Mater. 2006;54:1279–1288. doi:10.1016/j.actamat.2005.11.001.
31.
LiZChaiFYangCCo-precipitation mechanism of nanoscale particles and mechanical properties in multicomponent ultra-high strength low carbon steel. Mater Sci Eng A. 2019;748:128–136. doi:10.1016/j.msea.2019.01.086.
32.
YuY.Metallography principle. Beijing: Metallurgical Industry Press; 2013.
33.
VishnukumarMMuthupandiVJeromeS.Effect of post-heat treatment on the mechanical and corrosion behaviour of SS316L fabricated by wire arc additive manufacturing. Mater Lett. 2022;307:131015. doi:10.1016/j.matlet.2021.131015.
34.
CalcagnottoMPongeDDemirEOrientation gradients and geometrically necessary dislocations in ultrafine grained dual-phase steels studied by 2D and 3D EBSD. Mater Sci Eng A. 2010;527:2738–2746. doi:10.1016/j.msea.2010.01.004.
35.
TakayamaYSzpunarJA.Stored energy and Taylor factor relation in an Al–Mg–Mn alloy sheet worked by continuous cyclic bending. Mater Trans. 2005;45:2316–2325. doi:10.2320/matertrans.45.2316.
36.
ShiLCuiXJinGStudy on micro-mechanism of carbon atom diffusion in surface nanocrystallization low carbon alloy steel using molecular dynamics simulation. Vacuum. 2020;184:109889. doi:10.1016/j.vacuum.2020.109889.
37.
KanLYYeQBWangQHRefinement of Cu-M2C precipitates and improvement of strength and toughness by Ti microalloying in a Cu-bearing steel. Mater Sci Eng A. 2021;802:140678. doi:10.1016/j.msea.2020.140678.
38.
ChenWGaoPWangSStrengthening mechanisms of Nb and V microalloying high strength hot-stamped steel. Mater Sci Eng A. 2020;797:140115. doi:10.1016/j.msea.2020.140115.
39.
ZhangBGZhangXMLiuHT.Precipitation behavior of B2 and κ-carbide during aging and its effect on mechanical properties in Al-containing high strength steel. Mater Char. 2021;178:111291. doi:10.1016/j.matchar.2021.111291.
40.
ZengTZhangSShiXEffect of NbC and VC carbides on microstructure and strength of high-strength low-alloyed steels for oil country tubular goods. Mater Sci Eng A. 2021;824:141845. doi:10.1016/j.msea.2021.141845.
41.
GladmanT.Precipitation hardening in metals. Mater Sci Technol. 1999;15:30–36. doi:10.1179/026708399773002782.
42.
Klemm-TooleJBenzJvieiraIStrengthening mechanisms influenced by silicon content in high temperature tempered martensite and bainite. Mater Sci Eng A. 2020;786:139419. doi:10.1016/j.msea.2020.139419.
43.
TervoHKaijalainenAPallaspuroSLow-temperature toughness properties of 500MPa offshore steels and their simulated coarse-grained heat-affected zones. Mater Sci Eng A. 2020;773:138719. doi:10.1016/j.msea.2019.138719.
44.
ZhuZHanJLiH.Effect of alloy design on improving toughness for X70 steel during welding. Mater Des. 2015;88:1326–1333. doi:10.1016/j.matdes.2015.09.073.
45.
ShiYHanZ.Effect of weld thermal cycle on microstructure and fracture toughness of simulated heat-affected zone for a 800 MPa grade high strength low alloy steel. J Mater Process Technol. 2008;207:30–39. doi:10.1016/j.jmatprotec.2007.12.049.
46.
YangJDongHGXiaYQPrecipitation behavior of carbides and cryogenic toughness in heat-affected zone of high-Mn twinning-induced plasticity steel welded joint. J Manuf Process. 2021;68:716–727. doi:10.1016/j.jmapro.2021.06.003.