The equiaxed solidification of Al–20Cu alloy under different cooling rates was investigated using in-situ synchrotron X-ray radiography. The results showed that mean grain size increases rapidly at the early stage of solidification, then reaches the final grain size gradually. And the change of final mean grain size with cooling rate follows d = 4132.3 × R−0.86. In addition, the evolution of grain size in Al–20Cu alloy was also simulated by ProCAST software. The experimental and simulation results indicated that, in the range of the cooling rate (5.0–7.5 K min−1), the major factor influencing the final grain size is the maximum nucleation density, while the nucleation undercooling has an insignificant effect on the final grain size.
HydeKBNormanAFPrangnellPB.The effect of cooling rate on the morphology of primary Al3Sc intermetallic particles in Al-Sc alloys. Acta Mater. 2001; 49(8):1327–1337.
2.
FuJWYangYSGuoJJEffect of cooling rate on solidification microstructures in AISI 304 stainless steel. Mater Sci Technol. 2008; 24(8):941–944.
3.
PangSWuGLiuWEffect of cooling rate on the microstructure and mechanical properties of sand-casting Mg–10Gd–3Y–0.5Zr magnesium alloy. Mater Sci Eng A. 2013; 562:152–160.
4.
TangH-PWangQ-DLeiCEffect of cooling rate on microstructure and mechanical properties of an Al-5.0Mg-3.0Zn-1.0Cu cast alloy. J Alloys Compd. 2019; 801:596–608.
5.
LiangGAliYYouGEffect of cooling rate on grain refinement of cast aluminium alloys. Materialia. 2018; 3:113–121.
6.
BognoANguyen-ThiHReinhartGGrowth and interaction of dendritic equiaxed grains: in situ characterization by synchrotron X-ray radiography. Acta Mater. 2013; 61(4):1303–1315.
7.
WangBTanDLeeTLUltrafast synchrotron X-ray imaging studies of microstructure fragmentation in solidification under ultrasound. Acta Mater. 2018; 144:505–515.
8.
MathiesenRHArnbergLBleuetPCrystal fragmentation and columnar-to-equiaxed transitions in Al-Cu studied by synchrotron X-ray video microscopy. Metall Mater Trans A. 2006; 37(8):2515–2524.
9.
ShuaiSGuoEPhillionABFast synchrotron X-ray tomographic quantification of dendrite evolution during the solidification of Mg Sn alloys. Acta Mater. 2016; 118:260–269.
10.
WangTXuJXiaoTEvolution of dendrite morphology of a binary alloy under an applied electric current: an in situ observation. Phys Rev E. 2010; 81:042601.
11.
XuanZMaoFCaoZIn situ observation on the solidification of Sn-10Cu hyperperitectic alloy under direct current field by synchrotron microradiography. J Alloys Compd. 2017; 721:126–133.
12.
LiottiELuiAKumarSThe spatial and temporal distribution of dendrite fragmentation in solidifying Al-Cu alloys under different conditions. Acta Mater. 2016; 121:384–395.
13.
CaoFYangFKangHEffect of traveling magnetic field on solute distribution and dendritic growth in unidirectionally solidifying Sn-50 wt-%Pb alloy: an in situ observation. J Cryst Growth. 2016; 450:91–95.
14.
HuangHShuDFuYSynchrotron radiation X-ray imaging of cavitation bubbles in Al-Cu alloy melt. Ultrason Sonochem. 2014; 21(4):1275–1278.
15.
WangFEskinDMiJA synchrotron X-radiography study of the fragmentation and refinement of primary intermetallic particles in an Al-35Cu alloy induced by ultrasonic melt processing. Acta Mater2017; 141:142–153.
16.
SeoS-MKimI-SLeeJ-HGrain structure and texture evolutions during single crystal casting of the Ni-base superalloy CMSX-4. Met Mater Int. 2009; 15(3):391–398.
17.
MatacheGStefanescuDMPuscasuCInvestigation of solidification microstructure of single crystal CMSX-4 superalloy – experimental measurements and modelling predictions. Int J Cast Metal Res. 2015; 28(6):323–336.
18.
KundNKDuttaP.Numerical study of influence of oblique plate length and cooling rate on solidification and macrosegregation of A356 aluminum alloy melt with experimental comparison. J Alloys Compd. 2016; 678:343–354.
19.
SzeligaDKubiakKBurbelkoAAModelling of grain microstructure of IN-713C castings. Solid State Phenom. 2013; 197:83–88.
20.
KermanpurARappazMVarahramNThermal and grain-structure simulation in a land-based turbine blade directionally solidified with the liquid metal cooling process. Metall Mater Trans B. 2000; 31(6):1293–1304.
21.
LuoSYangGXiaoLEffect of the melt superheat on equiaxed solidification of Al-20 wt% Cu alloy investigated by in situ synchrotron radiography. J Cryst Growth. 2017; 476:38–44.
22.
BognoANguyen-ThiHBilliaBIn situ analysis of dendritic equiaxed microstructure formation in Al-Cu alloys by synchrotron X-ray radiography. Trans Indian Inst Met. 2009; 62(4-5):427–431.
23.
ZhuJWangTCaoFReal time observation of equiaxed growth of Sn-Pb alloy under an applied direct current by synchrotron microradiography. Mater Lett. 2012; 89:137–139.
24.
YangFChenZCaoFGrain nucleation and growth behavior of a Sn-Pb alloy affected by direct current: an in situ investigation. J Mater Sci Technol. 2017; 33:1134–1140.
25.
KurzWFisherDJ.Fundamentals of solidification. Switzerland: Trans Tech; 1989.