Six {Ni,Co}-based alloys containing TaC were oxidised at 1250°C. The mass variations files were exploited to follow the progress of the spallation of the oxide scales during cooling. The oxides formed on surface were characterised. On average, spallation started after a 300 K cooling, at higher temperature for the nickel-richest alloys than for the others. These results are discussed by considering the effect of the base element and the natures and thicknesses of the external oxides. Tantalum has a negative influence on the scales adherence. The thicker scales formed on the cobalt-richest alloys are less affected by spallation. The CrTaO4 oxide is more deleterious for the adherence of the external oxide scale when it is gathered at the interface.
YoungD.High temperature oxidation and corrosion of metals. Amsterdam: Elsevier Corrosion Series; 2008.
2.
PintBADiStefanoJRWrightIG.Oxidation resistance: one barrier to moving beyond Ni-base superalloys. Mater Sci Eng A. 2006; 415(1–2):255–263. doi: 10.1016/j.msea.2005.09.091
3.
Encinas-OropesaADrewGLHardyMCEffcts of oxidation and hot corrosion in a nickel disc alloy. Proceedings of the 11th International Symposium on Superalloys. 2008: 609–618.
4.
HagelWC.The oxidation of iron, nickel and cobalt-base alloys containing aluminum. Corrosion. 1965; 21(10):316–326. doi: 10.5006/0010-9312-21.10.316
5.
SuzukiAPollockTM.High-temperature strength and deformation of (/(’ two-phase Co–Al–W-base alloys.
6.
KleinLBauerANeumeierSHigh temperature oxidation of (/(’–strengthened Co–base superalloys. Corros Sci. 2011; 53(5):2027–2034. doi: 10.1016/j.corsci.2011.02.033
7.
KofstadP.High temperature corrosion. London: Elsevier Applied Science; 1988.
8.
BerthodPArandaLLemoineP.Oxide spallation during cooling from high temperatures affecting carbides-containing nickel-based alloys. part I: case of ternary Ni-Cr-C alloys with various carbides fractions. Mater Sci Indian J. 2009; 5(1):42–48.
9.
BerthodPArandaLVébertC.Oxide spallation during cooling from high temperatures affecting carbides-containing nickel-based alloys. part II: case of Ni–Cr–C alloys with addition of tantalum. Mater Sci Indian J. 2009; 5(1):49–54.
10.
BerthodP.Thermogravimetric study of oxide spallation for binary and ternary cobalt-based and iron-based alloys oxidized at high temperature. Open Corr J. 2009; 2:61–70. doi: 10.2174/1876503300902010061
11.
YoudelisWKwonO.Carbide phases in nickel-base superalloy: nucleation properties of MC type carbide. Met Sci. 1983; 17(8):385–388. doi: 10.1179/030634583790420673
12.
QinXZGuoJTYuanCDecomposition of primary MC carbide and its effects on the fracture behaviors of a cast Ni-base superalloy. Mater Sci Eng A. 2008; A485(1–2):74–79. doi: 10.1016/j.msea.2007.07.055
13.
LiXWWangLDongJSEffect of solidification condition and carbon content on the morphology of MC carbide in directionally solidified nickel-base superalloys. J Mater Sci Technol. 2014; 30(12):1296–1300. doi: 10.1016/j.jmst.2014.06.010
FeltenEJGreggRA.The physical metallurgy and oxidation characteristics of a cobalt-base superalloy, SM-302. ASM Trans Q. 1964; 57(4):804–822.
16.
WeiZWZhaoWXZhouJYMicrostructure evolution of K6509 cobalt-base superalloy for over-temperature. Procedia Eng. 2015; 99:1302–1310. doi: 10.1016/j.proeng.2014.12.663
17.
VandermousenRFViatourPDrapierJMDirectional solidification of cobalt-base superalloys. Cobalt. 1974; 1:6–12.
18.
BerthodPVébertCArandaL.Effect of dendritic orientation of the high temperature oxidation kinetic of tantalum-containing nickel-base alloys. J Mater Sci. 2007; 42:352–362. doi: 10.1007/s10853-006-1033-4
19.
BradleyEF.Superalloys: a technical guide. Metals Park: ASM International; 1988.
20.
DonachieMJDonachieSJ.Superalloys: a technical guide. 2nd editionMaterials Park: ASM International; 2002.
21.
BerthodPBernardJLLiébautC.Cobalt-chromium alloy for spinner cups in manufacture of mineral wool from silicate glass. International Patent WO 2001090429A1; 2001.
22.
BerthodPHimeurZPanteixPJ.Influences of the Co content and of the level of high temperature on the microstructure and oxidation of cast {Ni, Co}-based Cr-rich TaC-containing cast alloys. J Alloys Cpd. 2018; 739:447–456. doi: 10.1016/j.jallcom.2017.12.254
23.
BerthodPHimeurZ.Dependence on the chromium content of the high-temperature oxidation behavior of Ta-rich nickel-based cast alloys. Oxid Met. 2018; 90:135–151. doi: 10.1007/s11085-017-9828-z
24.
BerthodPGomisJPMedjahdiGA study of the dependence on the Co and Ni proportions of the oxidation at elevated temperature of TaC-strengthened {Ni and Co}-based cast superalloys. Mater Chem Phys. 2020; 251: https://doi.org/10.1016/j.matchemphys.2020.123088.
25.
BerthodPGomisJP.Improvement of the high temperature oxidation of TaC-strengthened Co(Cr)-based cast superalloys by the addition of nickel. Corr Eng Sci Technol. 2019; 55(2):118–126. doi: 10.1080/1478422X.2019.1699261
26.
Obigodi–NdjengG.High temperature oxidation and electrochemical investigations on nickel-base alloys. Doctor-Engineer dissertation. Technical Faculty of the Erlangen–Nürnberg University; (Germany) 2011.
27.
ConrathEBerthodP.Oxide spallation during post-isothermal high temperature oxidation cooling of Cr-rich cast alloys Highly Alloyed with Hf. Open Mater Sci J. 2016; 10:89–100. doi: 10.2174/1874088X01610010089
28.
YuBLiYNieYHigh temperature oxidation behavior of a novel cobalt-nickel-base superalloy. J Alloys Compds. 2018; 765:1148–1157. doi: 10.1016/j.jallcom.2018.06.275