In this paper, the microcrack evolution in DP590 dual-phase steel was observed by in-situ straining in straining transmission electron microscopy. It was found that a void initiated ahead of a main crack. After the load was applied, a thinned area was nucleated ahead of the void tip, and it grew gradually into shallow nanovoid, penetrating nanovoid, and then new void. Meanwhile, the old void connected with the main crack. The repetitions of the procedures resulted in the continuous propagation of a crack. Interaction between microcracks was observed. The propagation direction of one microcrack may change, affected by other microcracks. Voids were observed between microcracks and have a significant effect on the coalescence of microcracks.
KuziakRKawallaRWaenglerS.Advanced high strength steels for automotive industry. Arch Civil Mech Eng. 2008; 8(2):103–117. doi: 10.1016/S1644-9665(12)60197-6
2.
BouazizOZurobHHuangM.Driving force and logic of development of advanced high strength steels for automotive applications. Steel Res Int. 2013; 84(10):937–947.
3.
ShomeMTumuluruM.Welding and joining of advanced high strength steels (AHSS). Cambridge: Woodhead Publishing; 2015.
4.
ShawJRZuidemaBK.New high strength steels help automakers reach future goals for safety, affordability, fuel efficiency and environmental responsibility; 2001. (AE Technical Paper).
5.
DasDChattopadhyayPP.Influence of martensite morphology on the work-hardening behavior of high strength ferrite–martensite dual-phase steel. J Mater Sci. 2009; 44(11):2957–2965. doi: 10.1007/s10853-009-3392-0
6.
TakahashiM.Development of high strength steels for automobiles. Nippon Steel Techn Rep. 2003; 88(88):2–6.
7.
ChenQZChuWYWangYBIn situ TEM observations of nucleation and bluntness of nanocracks in thin crystals of 310 stainless steel. Acta Metall Mater. 1995; 43(12):4371–4376. doi: 10.1016/0956-7151(95)00122-C
8.
ZhongYXiaoFZhangJIn situ TEM study of the effect of M/A films at grain boundaries on crack propagation in an ultra-fine acicular ferrite pipeline steel. Acta Mater. 2006; 54(2):435–443. doi: 10.1016/j.actamat.2005.09.015
9.
FengZYangYChenYIn-situ TEM investigation of fracture process in an Al–Cu–Mg alloy. Mater Sci Eng A. 2013; 586:259–266. doi: 10.1016/j.msea.2013.08.013
10.
YaoTDuKHaoYIn-situ observation of deformation induced α″ phase transformation in a β-titanium alloy. Mater Lett. 2016; 182:281–284. doi: 10.1016/j.matlet.2016.07.021
11.
OkamotoPHeuerJLamNStress-induced amorphization at moving crack tips in NiTi. Appl Phys Lett. 1998; 73(4):473–475. doi: 10.1063/1.121904
12.
ZhengMZhangWWuKThe deformation and fracture behavior of SiCw/AZ91 magnesium matrix composite during in-situ TEM straining. J Mater Sci. 2003; 38(12):2647–2654. doi: 10.1023/A:1024486619379
13.
ChenKPanSZhuYIn situ observations of crack propagation in as-cast Cu-1.5 Fe-0.5 Co (wt%) alloy. Mater Sci Eng A. 2017; 706:211–216. doi: 10.1016/j.msea.2017.08.055
14.
LuYQiaoLChuW.TEM observation of martensite reverse transformation during loading in CuNiAl shape memory alloys. J Mater Sci Lett. 2001; 20(15):1397–1400. doi: 10.1023/A:1011639426945
15.
WangYGuoZMaRInvestigation of the microcrack evolution in a Ti-based bulk metallic glass matrix composite. Prog Nat Sci Mater Int. 2014; 24(2):121–127. doi: 10.1016/j.pnsc.2014.03.010
16.
ZhangZMaoMWangJNanoscale origins of the damage tolerance of the high-entropy alloy CrMnFeCoNi. Nat Commun. 2015; 6:10143. doi: 10.1038/ncomms10143
17.
Avramovic-CingaraGOsoskovYJainMEffect of martensite distribution on damage behaviour in DP600 dual phase steels. Mater Sci Eng A. 2009; 516(1–2):7–16. doi: 10.1016/j.msea.2009.03.055
18.
ParkKNishiyamaMNakadaNEffect of the martensite distribution on the strain hardening and ductile fracture behaviors in dual-phase steel. Mater Sci Eng A. 2014; 604:135–141. doi: 10.1016/j.msea.2014.02.058
19.
Al-AbbasiFMNemesJA.Characterizing DP-steels using micromechanical modeling of cells. Comput Mater Sci. 2007; 39(2):402–415. doi: 10.1016/j.commatsci.2006.07.003
20.
RiegerF.Work-hardening of dual-phase steel [PhD thesis]; 2015.
21.
KunduAFieldDP.Influence of plastic deformation heterogeneity on development of geometrically necessary dislocation density in dual phase steel. Mater Sci Eng A. 2016; 667:435–443. doi: 10.1016/j.msea.2016.05.022