This work presents friction hydro-pillar processing (FHPP) and tungsten inert gas (TIG) welding of SAF2205 duplex stainless steel. Weld microstructural and mechanical characterisation were carried out based on the standards (DNV-RP-F112 and DNV-OS-F101). Therefore, optical microscopy, scanning electron microscopy, energy dispersive X-ray spectroscopy, and X-ray diffraction were used. In addition, mechanical properties were evaluated by microhardness measurements. Furthermore, the joining processes were thermodynamically simulated for confirmation of the expected phases in each welding method. It was possible to verify the phases developed after the experimental welding (FHPP and TIG) as well as the ones obtained in the thermodynamic analyses. Finally, it was noted that FHPP promoted mechanical and metallurgical features requested by the standards.
JardimMP, GonçalvesRA, PaesMTP, Efeito da geometria do pino e do furo no reparo por atrito resultados preliminares. Tecnol Em Metal Mater E Min. 2007;4:27–32.
3.
LessaCRdeL, MartinazziD, FigueiredoAP, Microstructural behavior of SAF 2205 duplex stainless steel welded by friction Hydro Pillar processing. Mater Res. 2016;19:928–936. doi: 10.1590/1980-5373-MR-2016-0023
4.
YehFWT, Pereira da CunhaPHC, LessaCRdeL, Evaluation of discontinuities in A36 steel Repairs with friction Hydro Pillar processing using different axial forces. ISIJ Int. 2013;53:2269–2271. doi: 10.2355/isijinternational.53.2269
5.
FolkhardE.Welding metallurgy of stainless steels. New York: Springer-Verlag Wien; 1988.
6.
AmbroziakA, GulB.Investigations of underwater FHPP for welding steel overlap joints. Arch Civ Mech Eng. 2007;7:67–76. doi: 10.1016/S1644-9665(12)60212-X
7.
BlakemoreG.Friction welding - technology for the New Millennium. In: The Offshore Technology Conference; 1999.
8.
MeyerA, PaulyD, Dos SantosJF, Considerations on robotic friction stitch welding for the repair of marine structures, in: Proceedings of 20th International Conference on Offshore Mechanics and Arctic Engineering, 2001, pp. 145–151.
9.
SantosGM, FormosoCM, FrancoSD, Optimization of control parameters in a friction hydro pillar processing unit to repair oil steel structures. ABCM Symp Ser Mechatron. 2012;5:573–582.
10.
Alvarez-ArmasI, Degallaix-MoreuilS.Duplex stainless steels. John Wiley & Sons, Inc.; 2009.
11.
ColpaertH.Metallography of steels: interpretation of structure and the effects of processing. São Paulo, Brazil: 1a, ASM International; 2018.
PérezAFM, BredaM, CalliariI, Detrimental Cr-rich phases precipitation on SAF 2205 duplex stainless Steels welds after heat treatment. Soldag Insp. 2016;21:165–171. doi: 10.1590/0104-9224/SI2102.06
14.
VermaJ, TaiwadeRV.Effect of welding processes and conditions on the microstructure, mechanical properties and corrosion resistance of duplex stainless steel weldments—A review. J Manuf Process. 2017;25:134–152. doi: 10.1016/j.jmapro.2016.11.003
15.
GiorjãoRAR, PereiraVF, TeradaM, Microstructure and mechanical properties of friction stir welded 8 mm pipe SAF 2507 super duplex stainless steel. J Mater Res Technol. 2018.
16.
SaeidT, Abdollah-zadehA, AssadiH, Effect of friction stir welding speed on the microstructure and mechanical properties of a duplex stainless steel. Mater Sci Eng A. 2008;496:262–268. doi: 10.1016/j.msea.2008.05.025
17.
BaoshengZ, XiangdongJ, JiaqingC, Numerical simulation onto the preliminary period of friction hydro pillar processing in friction stitch welding; 2010.
18.
PaesMTP.Processamento termomecânico de pinos de aço no interior de cavidades de aço C-Mn através de soldagem por atrito rotacional, UFRJ; 2013.
19.
UnfriedJS, HermenegildoTF, PaesMTP, Influence of process parameters in the TMAZ microstructural evolution of C-Mn steels friction Hydro-Pillar welded joints. Tecnol Met Mater Min. 2009;6:73–79.
20.
DET NORSKE VERITAS AS, DNV-OS-F101 - Submarine Pipeline Systems, DNV; 2012.
21.
DET NORSKE VERITAS, DNV-RP-F112 - Design of Duplex Stainless Steel Subsea Equipment Exposed To Cathodic Protection, DNV; 2008.
22.
E04 Committee, ASMT-E1245 - Practice for Determining the Inclusion or Second-Phase Constituent Content of Metals by Automatic Image Analysis, ASTM International; 2008.
23.
E04 Committee, E562 − 11 - Standard Test Method for Determining Volume Fraction by Systematic Manual Point Count.pdf, ASTM International; 2011.
24.
E04 Committee, ASTM E112-13: Standard test methods for determining average grain size, ASTM International; n.d.
LessaCRdeL, CaregnatoMF, CunhaPHCPda, Microstructural evaluation of a C-Mn steel welded by the friction hidro-pillar process. Soldag Insp. 2011;16:02–11. doi: 10.1590/S0104-92242011000100002
28.
ChludzinskiM, PaesMP, BastianFL, Fracture toughness of friction Hydro-Pillar processing welding in C–Mn steel. Mater Des. 2012;33:340–344. doi: 10.1016/j.matdes.2011.07.056
29.
MeinhardtCP, ChludzinskiM, RibeiroRF, Evaluation of friction hydro-pillar processing welding in duplex stainless steels (UNS S31803). J Mater Process Technol. 2017;246:158–166. doi: 10.1016/j.jmatprotec.2017.03.010
30.
EscribaDM, Materna-MorrisE, PlautRL, Chi-phase precipitation in a duplex stainless steel. Mater Charact. 2009;60:1214–1219. doi: 10.1016/j.matchar.2009.04.013
31.
ChenTH, WengKL, YangJR.The effect of high-temperature exposure on the microstructural stability and toughness property in a 2205 duplex stainless steel. Mater Sci Eng A. 2002;338:259–270. doi: 10.1016/S0921-5093(02)00093-X
32.
GustafsonP.A thermodynamic evaluation of the Cr-Ni-W system. Calphad. 1988;12:277–292. doi: 10.1016/0364-5916(88)90008-9
33.
QiuC.An analysis of the Cr-Fe-Mo-C system and modification of thermodynamic parameters. ISIJ Int. 1992;32:1117–1127. doi: 10.2355/isijinternational.32.1117
34.
UreñaA, OteroE, UtrillaMV, Weldability of a 2205 duplex stainless steel using plasma arc welding. J Mater Process Technol. 2007;182:624–631. doi: 10.1016/j.jmatprotec.2006.08.030
35.
LippoldJC, VarolI, BaeslackW.IIIThe influence of composition and microstructure on the HAZ toughness of duplex stainless steels at −20C. Weld J. 1994;73(4):S75–S79.
36.
TottenG.Steel heat treatment: metallurgy and technologies. Portland: Taylor & Francis Group, LLC; 2006.
37.
MoraesCAPd, ChludzinskiM, NunesRM, Residual stress evaluation in API 5L X65 girth welded pipes joined by friction welding and gas tungsten arc welding. J Mater Res Technol. 2018.
38.
SbalchieroJA, MartinazziD, LemosGVB, Replacement of Gas Metal Arc welding by friction welding for joining tubes in the Hydraulic Cylinders industry. Mater Res. 2018;21:1–8. doi: 10.1590/1980-5373-mr-2018-0015
39.
SieurinH, SandströmR.Sigma phase precipitation in duplex stainless steel 2205. Mater Sci Eng A. 2007;444:271–276. doi: 10.1016/j.msea.2006.08.107
40.
Llorca-IsernN, López-LuqueH, López-JiménezI, Identification of sigma and chi phases in duplex stainless steels. Mater Charact. 2016;112:20–29. doi: 10.1016/j.matchar.2015.12.004