The present work reports the effect of different initial microstructures on reverse transformation kinetics and morphologies of austenite formed during intercritical annealing in Fe-0.14C-7Mn-1Si (wt-%) medium Mn steel. Three different initial microstructures were produced by cold-rolling and cold-rolling followed by austenitisation at 820°C and 900°C. The specimen austenitised at higher temperature shows lath-type austenite after intercritical annealing. The difference in austenitisation temperature leads to different Mn distribution in martensitic initial microstructures, thereby leading to a difference in morphology of austenite. The inhomogeneous Mn profiles in initial microstructures also affect reverse transformation kinetics of austenite upon intercritical annealing. The presence of Mn-enriched regions accelerates austenite growth at an early stage of intercritical annealing but retards the transformation kinetics afterwards.
This paper is part of a Thematic Issue on Medium Manganese Steels.
BhadeshiaH, HoneycombeR.Steels: microstructure and properties. Oxford: Butterworth-Heinemann; 2006.
2.
De CoomanBC.Structure–properties relationship in TRIP steels containing carbide-free bainite. Curr Opin Solid State Mater Sci. 2004;8(3–4):285–303. doi: 10.1016/j.cossms.2004.10.002
3.
ChungJH, JeonJB, ChangYW.Work-hardening and ductility enhancement mechanism of cold rolled multiphase TRIP steels. Met Mater Int. 2010;16(4):533–541. doi: 10.1007/s12540-010-0803-3
4.
ZaeffererS, OhlertJ, BleckW.A study of microstructure, transformation mechanisms and correlation between microstructure and mechanical properties of a low alloyed TRIP steel. Acta Mater. 2004;52(9):2765–2778. doi: 10.1016/j.actamat.2004.02.044
5.
JacquesPJ.Transformation-induced plasticity for high strength formable steels. Curr Opin Solid State Mater Sci. 2004;8(3–4):259–265. doi: 10.1016/j.cossms.2004.09.006
6.
MillerRL.Ultrafine-grained microstructures and mechanical properties of alloy steels. Metall Trans. 1972;3(4):905–912. doi: 10.1007/BF02647665
7.
FurukawaT.Dependence of strength–ductility characteristics on thermal history in lowcarbon, 5 wt-%Mn steels. Mater Sci Technol. 1989;5(5):465–470. doi: 10.1179/mst.1989.5.5.465
8.
SuhD-W, ParkS-J, LeeT-H, Influence of Al on the microstructural evolution and mechanical behavior of low-carbon, manganese transformation-induced-plasticity steel. Metall Mater Trans A. 2010;41(2):397. doi: 10.1007/s11661-009-0124-7
9.
CaoWQ, WangC, ShiJ, Microstructure and mechanical properties of Fe–0.2C–5Mn steel processed by ART-annealing. Mater Sci Eng A. 2011;528(22–23):6661–6666. doi: 10.1016/j.msea.2011.05.039
10.
HanJ, LeeS-J, JungJ-G, The effects of the initial martensite microstructure on the microstructure and tensile properties of intercritically annealed Fe–9Mn–0.05C steel. Acta Mater. 2014;78:369–377. doi: 10.1016/j.actamat.2014.07.005
11.
LeeYK, HanJ.Current opinion in medium manganese steel. Mater Sci Technol. 2015;31:843–856. doi: 10.1179/1743284714Y.0000000722
12.
ArlazarovA, GounéM, BouazizO, Evolution of microstructure and mechanical properties of medium Mn steels during double annealing. Mater Sci Eng A. 2012;542:31–39. doi: 10.1016/j.msea.2012.02.024
13.
SugimotoK-i, IidaT, SakaguchiJ, Retained austenite characteristics and tensile properties in a TRIP type bainitic sheet steel. ISIJ Int. 2000;40(9):902–908. doi: 10.2355/isijinternational.40.902
14.
KimJI, RyuJH, LeeSW, Influence of the initial microstructure on the reverse transformation kinetics and microstructural evolution in transformation-induced plasticity–assisted steel. Metall Mater Trans A. 2016;47(11):5352–5361. doi: 10.1007/s11661-016-3672-7
15.
SugimotoK-i, NakanoK, SongS-M, Retained austenite characteristics and stretch-flangeability of high-strength Low-alloy TRIP type bainitic sheet steels. ISIJ Int. 2002;42(4):450–455. doi: 10.2355/isijinternational.42.450
16.
KimJI, ChoiYH, RyuJH, Influence of heating rate on annealing and reverse transformation behavior of TRIP steels having martensite as starting microstructure. Metall Mater Trans A. 2017;48(11):5217–5222. doi: 10.1007/s11661-017-4331-3
17.
LeeB, SundmanB.Tcfe2000: The thermo-calc steels database. Stockholm: KTH; 1999.
18.
JoenssonB.On ferromagnetic ordering and lattice diffusion. A simple model. Z. Metallkd. 1992;83:349–355.
19.
FridbergJ, TorndahlL-E, HillertM.Diffusion in Iron. Jernkont Ann. 1969;153:263–276.
20.
KoistinenDP, MarburgerRE.A general equation prescribing the extent of the austenite-martensite transformation in pure iron-carbon alloys and plain carbon steels. Acta Metall. 1959;7(1):59–60. doi: 10.1016/0001-6160(59)90170-1
21.
MahieuJ, De CoomanBC, MakiJ.Phase transformation and mechanical properties of si-free CMnAl transformation-induced plasticity-aided steel. Metall Mater Trans A. 2002;33(8):2573–2580. doi: 10.1007/s11661-002-0378-9
22.
ArlazarovA, GounéM, BouazizO, Critical factors governing the thermal stability of austenite in an ultra-fined grained medium-Mn steel. Philos Mag Lett. 2017;97(4):125–131. doi: 10.1080/09500839.2017.1290293
23.
LeeS, De CoomanBC.On the selection of the optimal intercritical annealing temperature for medium Mn TRIP steel. Metall Mater Trans A. 2013;44(11):5018–5024. doi: 10.1007/s11661-013-1860-2
24.
WeiR, EnomotoM, HadianR, Growth of austenite from as-quenched martensite during intercritical annealing in an Fe–0.1 C–3Mn–1.5 Si alloy. Acta Mater. 2013;61(2):697–707. doi: 10.1016/j.actamat.2012.10.019