The effect of Sc on the microstructure and mechanical properties of Al–Si–Mg–Cu–Ti alloy was investigated. Results obtained in this research indicate that, with increasing Sc content, the microstructure of the investigated alloys exhibits finer equiaxed dendrites with rounded edges and the morphology of the eutectic Si shows a complete transition from a coarse needle-like structure to a fine fibrous structure upon modification of eutectic Si. Subsequent T6 heat treatment had further induced the precipitation of nano-scaled secondary Al3(Sc, Ti) phase, as well as spheroidisation of eutectic Si. Combined with T6 heat treatment, the ultimate tensile strength, yield strength, percentage elongation and hardness were achieved in 0.20 wt-% Sc-modified alloy.
LiuZ, ChengN, ZhengQ, Processing and tensile properties of A356 composites containing in situ small-sized Al3Ti particulates. Mater. Sci. Eng. A. 2018;710:392–399. doi: 10.1016/j.msea.2017.11.005
2.
PramodS, RaoA, MurtyB, Effect of Sc addition on the microstructure and wear properties of A356 alloy and A356–TiB2 in situ, composite. Mater. Des. 2015;78:85–94. doi: 10.1016/j.matdes.2015.04.026
3.
ChomsaengN, HarutaM, ChairuangsriT, HRTEM and ADF-STEM of precipitates at peak-ageing in cast A356 aluminium alloy. J. Alloys Compd. 2010;496(1–2):478–487. doi: 10.1016/j.jallcom.2010.02.084
4.
PatakhamU, KajornchaiyakulJ, LimmaneevichitrC.Modification mechanism of eutectic silicon in Al–6Si–0.3Mg alloy with scandium. J. Alloys Compd. 2013;575(15):273–284. doi: 10.1016/j.jallcom.2013.05.139
5.
PramodS.R, RaoA, Effect of Sc addition and T6 aging treatment on the microstructure modification and mechanical properties of A356 alloy. Mater. Sci. Eng. A. 2016;674:438–450. doi: 10.1016/j.msea.2016.08.022
6.
XuC, XiaoW, HanadaS, The effect of scandium addition on microstructure and mechanical properties of Al–Si–Mg alloy: A multi-refinement modifier. Mater. Charact. 2015;110:160–169. doi: 10.1016/j.matchar.2015.10.030
7.
YıldırımM, ÖzyürekD.The effects of Mg amount on the microstructure and mechanical properties of Al–Si–Mg alloys. Mater. Des. 2013;51(5):767–774. doi: 10.1016/j.matdes.2013.04.089
8.
AzadiM, ShirazabadM.Heat treatment effect on thermo-mechanical fatigue and low cycle fatigue behaviors of A356.0 aluminum alloy. Mater. Des. 2013;45:279–285. doi: 10.1016/j.matdes.2012.08.066
9.
LiP, LiuS, ZhangL, Grain refinement of A356 alloy by Al–Ti–B–C master alloy and its effect on mechanical properties. Mater. Des. 2013;47(9):522–528. doi: 10.1016/j.matdes.2012.12.033
10.
XiaoQ, LiuH, YiD, Effect of Cu content on precipitation and age-hardening behavior in Al–Mg–Si–xCu alloys. J. Alloys Compd. 2017;695:1005–1013. doi: 10.1016/j.jallcom.2016.10.221
11.
ChenZ, LeiY, ZhangH.Structure and properties of nanostructured A357 alloy produced by melt spinning compared with direct chill ingot. J. Alloys Compd. 2011;509(27):7473–7477. doi: 10.1016/j.jallcom.2011.04.082
12.
WangM, DuX, LiY, Effect of Sc on as-cast microstructures and mechanical properties of Al–Si–Mg–Cu–Ti alloys. Key Eng. Mater. 2017;732:32–37. doi: 10.4028/www.scientific.net/KEM.732.32
13.
ZhangZ, HosodaS, KimI, Grain refining performance for Al and Al–Si alloy casts by addition of equal-channel angular pressed Al–5 mass% Ti alloy. Mater. Sci. Eng. A. 2006;425(1–2):55–63. doi: 10.1016/j.msea.2006.03.018
14.
LiuC, LaiY, ChenJ, Natural-aging-induced reversal of the precipitation pathways in an Al–Mg–Si alloy. Scr. Mater. 2016;115:150–154. doi: 10.1016/j.scriptamat.2015.12.027
15.
BasavakumarK, MukundaP, ChakrabortyM.Influence of grain refinement and modification on microstructure and mechanical properties of Al–7Si and Al–7Si–2.5Cu cast alloys. Mater. Charact. 2008;59(3):283–289. doi: 10.1016/j.matchar.2007.01.011
16.
SjölanderE, SeifeddineS.The heat treatment of Al–Si–Cu–Mg casting alloys. J. Mater. Process. Technol. 2010;210(10):1249–1259. doi: 10.1016/j.jmatprotec.2010.03.020
17.
SadeghiI, WellsM, EsmaeiliS.Effect of particle shape and size distribution on the dissolution behavior of Al2Cu particles during homogenization in aluminum casting alloy Al–Si–Cu–Mg. J. Mater. Process. Technol.2017;251:232–240. doi: 10.1016/j.jmatprotec.2017.08.042
18.
DengY, YinZ, ZhaoK, Effects of Sc and Zr microalloying additions on the microstructure and mechanical properties of new Al–Zn–Mg alloys. J. Alloys Compd. 2012;530(7):71–80. doi: 10.1016/j.jallcom.2012.03.108
19.
DalenM, GygerT, DunandD, Effects of Yb and Zr microalloying additions on the microstructure and mechanical properties of dilute Al–Sc alloys. Acta Mater. 2011;59(20):7615–7626. doi: 10.1016/j.actamat.2011.09.019
20.
MukhopadhyayA, KumarA, RaveendraS, Development of grain structure during superplastic deformation of an Al–Zn–Mg–Cu–Zr alloy containing Sc. Scr. Mater. 2011;64(5):386–389. doi: 10.1016/j.scriptamat.2010.10.038
21.
PanD, ZhouS, ZhangZ, Effect of Sc(Zr) on the microstructure and mechanical properties of as-cast Al–Mg alloys. Mater. Sci. Tech. 2017;33:751–757. doi: 10.1080/02670836.2016.1270573
22.
ArfanM, CongX, WangX, High strength aluminum cast alloy: A Sc modification of a standard Al–Si–Mg cast alloy. Mater. Sci. Eng. A. 2014;604(604):122–126.
23.
SohiM, PooleW, SinclairC, Yield strength of twin-belt cast Al–Mg–Sc–Zr alloy after annealing. Mater. Sci. Tech. 2015;31(4):460–467. doi: 10.1179/1743284714Y.0000000629
24.
KilicaslanM, LeeW, LeeT, Effect of Sc addition on the microstructure and mechanical properties of as-atomized and extruded Al–20Si alloys. Mater. Lett. 2012;71(71):164–167. doi: 10.1016/j.matlet.2011.12.050
25.
CeschiniL, MorriA, MorriA, Correlation between ultimate tensile strength and solidification microstructure for the sand cast A357 aluminium alloy. Mater. Des. 2009;30(10):4525–4531. doi: 10.1016/j.matdes.2009.05.012
26.
LiuX, ZhangY, BeausirB, Twin-controlled growth of eutectic Si in unmodified and Sr-modified Al–12.7% Si alloys investigated by SEM/EBSD. Acta Mater. 2015;97:338–347. doi: 10.1016/j.actamat.2015.06.041