The reaction path of the (Ti0.9, Mo0.1)2AlC phase from Ti, Al, TiC and Mo powder mixtures was investigated in detail ranging from 500 to 1450°C, and the results show that the reaction between Ti and Al produced Ti–Al intermetallics, and the reaction between Al and Mo formed Mo–Al intermetallics. And then the (Ti0.9, Mo0.1)2AlC phase was formed by the reaction of Ti–Al, Mo–Al intermetallics, and TiC. At 1350°C for 2 h, a dense (Ti0.9, Mo0.1)2AlC phase with purity was successfully fabricated. The Vickers hardness, flexural strength and fracture toughness were 5.48 GPa, 363.60 MPa and 5.78 MPa m1/2, which were improved by 44, 34 and 136% for (Ti0.80, Mo0.20)2AlC, respectively, compared with the single-phase Ti2AlC.
BarsoumMW.The Mn+1AXn phases: a new class of solids thermodynamically stable nanolaminates. Prog Solid State Chem. 2000;28:201–281. doi: 10.1016/S0079-6786(00)00006-6
2.
BarsoumMW, BrodkinD, El-RaghyT.Layered machinable ceramics for high temperature applications. Scrip Mater. 1997;36:535–541. doi: 10.1016/S1359-6462(96)00418-6
3.
SunZM, MurugaiahA, ZhenT, Microstructure and mechanical properties of porous Ti3SiC2. Acta Mater. 2005;53:4359–4366. doi: 10.1016/j.actamat.2005.05.034
4.
EklundP, BeckersM, JanssonU, The Mn+1AXn phases: materials science and thin-film processing. Thin Solid Films. 2010;518:1851–1878. doi: 10.1016/j.tsf.2009.07.184
5.
EklundP, RosenJ, PerssonP.Layered ternary Mn+1AXn phases and their 2D derivative MXene: an overview from a thin-film perspective. J Phys D: Appl Phys. 2017;50:113001. doi: 10.1088/1361-6463/aa57bc
6.
ScabaroziTH, GennaouiC, RocheJ, Combinatorial investigation of (Ti1−xNbx)2AlC.Appl Phys Lett. 2009;95:101907. doi: 10.1063/1.3207748
7.
BarsoumMW, SalamaI, El-raghyT, Thermal and electrical properties of Nb2AlC, (Ti, Nb)2AlC and Ti2AlC. Metall Mater Trans A. 2002;33:2775–2779. doi: 10.1007/s11661-002-0262-7
8.
SalamaI, El-RaghyT, BarsoumMW.Synthesis and mechanical properties of Nb2AlC and (Ti, Nb)2AlC. J Alloy Compd. 2002;347:271–278. doi: 10.1016/S0925-8388(02)00756-9
9.
PhatakNA, SaxenaSK, FeiYW, Synthesis of a new MAX compound (Cr0.5V0.5)2GeC and its compressive behavior up to 49 GPa. J Alloy Compd. 2009;475:629–634. doi: 10.1016/j.jallcom.2008.07.102
10.
CabiochT, EklundP, MauchampV, Tailoring of the thermal expansion of Cr2(AlX,Ge1−X
)C phases. J Eur Ceram Soc. 2013;33:897–904. doi: 10.1016/j.jeurceramsoc.2012.10.008
11.
MengFL, ZhouYC, WangJY.Strengthening of Ti2AlC by substituting Ti with V. Scripta Mater. 2005;53:1369–1372. doi: 10.1016/j.scriptamat.2005.08.030
12.
GuptaS, BarsoumMW.Synthesis and oxidation of V2AlC and (Ti0.5,V0.5)(2)AlC in air. J Electrochem Soc. 2004;151:D24–D29. doi: 10.1149/1.1639160
13.
ZhengLY, WangJM, LuXP, (Ti0.5Nb0.5)5AlC4: ‘a new-layered compound belonging to MAX phases’. J Am Ceram Soc. 2010;93:3068–3071. doi: 10.1111/j.1551-2916.2010.04056.x
14.
ZhouYC, MengFL, ZhangJ.New MAX-phase compounds in the V-Cr-Al-C system. J Am Ceram Soc. 2008;91:1357–1360. doi: 10.1111/j.1551-2916.2008.02279.x
15.
AnasoriB, DahlqvistM, HalimJ, Experimental and theoretical characterization of ordered MAX phases Mo2TiAlC2 and Mo2Ti2AlC3. J Appl Phys. 2015;118:094304. doi: 10.1063/1.4929640
16.
AnasoriB, HalimJ, LuJ, Mo2TiAlC2: a new ordered layered ternary carbide. Scripta Mater. 2015;101:5–7. doi: 10.1016/j.scriptamat.2014.12.024
17.
LiY, LiuN, ZhangXB, Effect of Mo addition on the microstructure and mechanical properties of ultra-fine grade TiC-TiN-WC-Mo2C-Co cermets. Int J Refrct Met Hard Mater. 2008;26:190–196. doi: 10.1016/j.ijrmhm.2007.05.005
18.
SchneibelJH, RawnnCJ, PayzantEA, Controlling the thermal expansion anisotropy of Mo5Si3 and Ti5Si3 silicides. Intermetallics. 2004;12:845–850. doi: 10.1016/j.intermet.2004.02.035
19.
ZhuJF, PanRJ, WangF.Effect of MoO3 addition on the microstructure and mechanical properties of Ti2A1C prepared by reactive hot pressing. J Mater Res. 2013;28:2164–2170. doi: 10.1557/jmr.2013.215
20.
LiuGH, ChenKX, ZhouHP, Layered growth of Ti2AlC and Ti3AlC2 in combustion synthesis. Mater Lett. 2007;61:779–784. doi: 10.1016/j.matlet.2006.05.060
21.
PietzkaMA, SchusterJC.Summary of constitutional data on the aluminum–carbon–-titanium system. J Phase Equilib. 1994;15:392–400. doi: 10.1007/BF02647559
22.
WangJY, ZhouYC.Ab initio elastic stiffness of nano-laminate (MxM'2−x)AlC (M and M’ = Ti, V and Cr) solid solution. J Phys: Condens Matter. 2004;16:2819–2827.
23.
WangXH, ZhouYC.Microstructure and properties of Ti3AlC2 prepared by the solid–liquid reaction synthesis and simultaneous in-situ hot pressing process. Acta Mater. 2002;50:3141–3149.
24.
HanJH, HwangSS, LeeDY, Synthesis and mechanical properties of Ti3AlC2 by hot pressing TiCx/Al powder mixture. J Eur Ceram Soc. 2008;28:979–988. doi: 10.1016/j.jeurceramsoc.2007.09.015