The uniaxial tensile tests of Hastelloy C-276 were performed under elevated temperature and strain rate. Considering the effects of different deformation parameters, the flow behaviour, microstructure and fracture characteristics were analysed based on the experimental data. From the rheological curves, the typical characteristics of dynamic recrystallisation were observed at a relatively high deformation temperature and low strain rate. Optical microstructures show that the degree of dynamic recrystallisation increases with an increase in temperature. The SEM micrographs show that the amount of precipitates increases with an increase in deformation temperature. Examination of the fracture morphology at high magnifications revealed that the coalescence of microscopic voids is responsible for the fracture failure.
ZhuZ, ZhangL, WuQ, An experimental investigation of thermal contact conductance of Hastelloy C-276 based on steady-state heat flux method. Int Commun Heat Mass Transfer. 2013;41:63–67. doi: 10.1016/j.icheatmasstransfer.2012.11.007
ZhangQ, TangR, YinK, Corrosion behavior of Hastelloy C-276 in supercritical water. Corros Sci. 2009;51:2092–2097. doi: 10.1016/j.corsci.2009.05.041
4.
Mohammadi ShoreF, MorakabatiM, AbbasiSM, Hot deformation behavior of Incoloy 901 through hot tensile testing. J Mater Eng Perform. 2014;23:1424–1433. doi: 10.1007/s11665-014-0863-5
5.
LiuY, NingY, YangX, Effect of temperature and strain rate on the workability of FGH4096 superalloy in hot deformation. Mater Des. 2016;95:669–676. doi: 10.1016/j.matdes.2016.01.032
6.
WangJ, LiuD, HuY, Effect of grain size distribution on processing maps for isothermal compression of Inconel 718 superalloy. J Mater Eng Perform. 2016;25:677–686. doi: 10.1007/s11665-016-1887-9
7.
WuK, LiuGQ, HuBF, Effect of processing parameters on hot compressive deformation behavior of a new Ni–Cr–Co based P/M superalloy. Mater Sci Eng A. 2011;528:4620–4629. doi: 10.1016/j.msea.2011.02.051
8.
WuK, LiuG, HuB, Characterization of hot deformation behavior of a new Ni–Cr–Co based P/M superalloy. Mater Charact. 2010;61:330–340. doi: 10.1016/j.matchar.2009.12.013
9.
NingY, YaoZ, FuMW, Recrystallization of the hot isostatic pressed nickel-base superalloy FGH4096: I. microstructure and mechanism. Mater Sci Eng A. 2011;528:8065–8070. doi: 10.1016/j.msea.2011.07.053
10.
ChenX, LinYC, ChenM, Microstructural evolution of a nickel-based superalloy during hot deformation. Mater Des. 2015;77:41–49. doi: 10.1016/j.matdes.2015.04.004
11.
GuoS, LiD, PenH, Hot deformation and processing maps of Inconel 690 superalloy. J Nucl Mater. 2011;410:52–58. doi: 10.1016/j.jnucmat.2010.12.309
12.
YangL, ZhuG, DongJ, Hot deformation characteristics and forging process of corrosion resistant nickel-base C-276 alloy. Procedia Eng. 2012;27:1008–1015. doi: 10.1016/j.proeng.2011.12.548
13.
ZhangC, ZhangL, ShenW, Characterization of hot deformation behavior of Hastelloy C-276 using constitutive equation and processing Map. J Mater Eng Perform. 2015;24:149–157. doi: 10.1007/s11665-014-1310-3
14.
WenD, LinYC, LiH, Hot deformation behavior and processing map of a typical Ni-based superalloy. Mater Sci Eng A. 2014;591:183–192. doi: 10.1016/j.msea.2013.09.049
15.
ChenX, LinYC, WenD, Dynamic recrystallization behavior of a typical nickel-based superalloy during hot deformation. Mater Des. 2014;57:568–577. doi: 10.1016/j.matdes.2013.12.072
16.
HutchinsonJW, NealeKW.Influence of strain-rate sensitivity on necking under uniaxial tension. Acta Metall. 1977;25:839–846. doi: 10.1016/0001-6160(77)90168-7
17.
HuangY, LinYC, DengJ, Hot tensile deformation behaviors and constitutive model of 42CrMo steel. Mater Des. 2014;53:349–356. doi: 10.1016/j.matdes.2013.06.070
18.
ThomasA, El-WahabiM, CabreraJM, High temperature deformation of Inconel 718. J Mater Process Technol. 2006;177:469–472. doi: 10.1016/j.jmatprotec.2006.04.072
19.
XiaoZ, HuangY, LiuH, Hot tensile and fracture behavior of 35CrMo steel at elevated temperature and strain rate. Metals (Basel). 2016;6:210. doi: 10.3390/met6090210
20.
JosephC, PerssonC, Hörnqvist CollianderM.Influence of heat treatment on the microstructure and tensile properties of Ni-base superalloy Haynes 282. Mater Sci Eng A. 2017;679:520–530. doi: 10.1016/j.msea.2016.10.048
21.
BaiG, LiJ, HuR, Effect of thermal exposure on the stability of carbides in Ni–Cr–W based superalloy. Mater Sci Eng A. 2011;528:2339–2344. doi: 10.1016/j.msea.2010.11.088
22.
BaiG, LiJ, HuR, Effect of temperature on tensile behavior of Ni–Cr–W based superalloy. Mater Sci Eng A. 2011;528:1974–1978. doi: 10.1016/j.msea.2010.11.053
23.
LinYC, DengJ, JiangY, Hot tensile deformation behaviors and fracture characteristics of a typical Ni-based superalloy. Mater Des. 2014;55:949–957. doi: 10.1016/j.matdes.2013.10.071