Reverse transformation of strain-induced martensite (SIM) was studied in the 18Cr–8Ni stainless steel. Microstructure analysis was performed on samples in an as-deformed state and after reversion annealing at 873 and 973 K, using the transmission Kikuchi diffraction. The primary, as well as reversed, austenite possesses the Kurdjumov–Sachs crystallographic orientation relationship, with respect to the SIM. The reverted austenite keeps one orientation within all reverted grains, regardless of the applied heating procedure, where the amount of reverted austenite depends only on the annealing temperature.
OlsonGB, CohenM.A mechanism for the strain-induced nucleation of martensitic transformations. J Less Common Met. 1972;28:107–118. doi: 10.1016/0022-5088(72)90173-7
2.
SandersonG, LlewellynD.Mechanical properties of standard austenitic stainless steels in the temperature range -196 to + 800°C. J Iron Steel Inst. 1969;207: 1129–1140.
3.
MangononPL, ThomasG.The martensite phases in 304 stainless steel. Metall Trans A. 1970;1(6):1577–1586. doi: 10.1007/BF02642003
4.
MangononPL, ThomasG.Structure and properties of thermal-mechanically treated 304 stainless steel. Metall Trans A. 1970;1(6):1587–1594. doi: 10.1007/BF02642004
5.
FahrD.Stress- and strain-induced formation of martensite and its effects on strength and ductility of metastable austenitic stainless steels. Metall Trans A. 1971;2(7):1883–1892.
6.
BogersAJ, BurgersWG.Partial dislocations on the {110} planes in the B.C.C. lattice and the transition of the F.C.C. into the B.C.C. lattice. Acta Metall. 1964;12(2):255–261. doi: 10.1016/0001-6160(64)90194-4
7.
Xu-ShengY, ShengS, Xiao-LeiW, Dissecting the mechanism of martensitic transformation via atomic-scale observations. Sci Rep. 2014;4:6141.
8.
TomimuraK, TakakiS, TokunagaY.Reversion mechanism from deformation induced martensite to austenite in metastable austenitic stainless steels. ISIJ Int. 1991;31(12):1431–1437. doi: 10.2355/isijinternational.31.1431
9.
TomimuraK, TakakiS, TanimotoS, Optimal chemical composition in Fe-Cr-Ni alloys for ultra grain refining by reversion from deformation induced martensite. ISIJ Int. 1991;31(7):721–727. doi: 10.2355/isijinternational.31.721
10.
SantosTFA, AndradeMS.Dilatometric evaluation of strain-induced martensite reversion in type AISI 304 austenitic stainless steel. Materia (Rio J). 2008;13(4):587–596. doi: 10.1590/S1517-70762008000400003
11.
GhoshSK, MallickP, ChattopadhyayPP.Effect of reversion of strain induced martensite on microstructure and mechanical properties in an austenitic stainless steel. J Mater Sci. 2011;46(10):3480–3487. doi: 10.1007/s10853-011-5253-x
12.
MisraRDK, NayakS, MaliSA, On the significance of nature of strain-induced martensite on phase-reversion-induced nanograined/ultrafine-grained aust-enitic stainless steel. Metall Mater Trans A. 2010;41(1):3–12. doi: 10.1007/s11661-009-0072-2
13.
SchinoA.D, SalvatoriI, KennyJM.Effects of martensite formation and austenite reversion on grain refining of AISI 304 stainless steel. J Mater Sci. 2002;37:4561–4565. doi: 10.1023/A:1020631912685
14.
ForouzanF, NajaflzadehA, KermanpurA, Artificial neural network models for production of nano-grained structure in AISI 304L stainless steel by predicting thermomechanical parameter. ISIJ Int. 2009;6(2):6–13.
15.
RajasekharaS, KarjalainenLP, KyrolainenA, Microstructure evolution in nano/submicron grained AISI 301LN stainless steel. Mat Sci Eng A. 2010;527:1986–1996. doi: 10.1016/j.msea.2009.11.037
16.
RezaeeA, NajaflzadehA, KermanpurA, The influence of reversion annealing behaviour on the formation of nanograined structure in AISI 201L austenitic stainless steel through martensite treatment. Mater Des. 2011;32(8-9):4437–4442. doi: 10.1016/j.matdes.2011.03.065
17.
SunGS, DuLX, HuJ, Ultrahigh strength nano/ultra fine-grained 304 stainless steel through three-stage cold rolling and annealing treatment. Mater Charact. 2015;110:228–235. doi: 10.1016/j.matchar.2015.11.001
18.
GongN, WuHB, NiuG, Effects of annealing temperature on nano/ultrafine-grained structure in austenite stainless steel. Mater Sci Tech. 2017;6. doi: 10.1080/02670836.2017.1310442.
19.
YagodzinskyyY, PimenoffJ, TarasenkoO, Grain refinement processes for superplastic forming of AISI 304 and 304L austenitic stainless steels. Mater Sci Tech. 2004;20(7):925–929. doi: 10.1179/026708304225019678
20.
ForouzanF, NajaflzadehA, KermanpurA, Production of nano/submicron grained AISI 304L stainless steel through the martensite reversion process. Mat Sci Eng A. 2010;527(27):7334–7339. doi: 10.1016/j.msea.2010.08.002
21.
WuHB, WuFJ, YangSW, The formation mechanism of austenite structure with micro/sub-micrometer bimodal grain size distribution. Acta Metall Sin. 2014;50(3):269274.
22.
WuH, NiuG, CaoJ, Annealing of strain-induced martensite to obtain micro/nanometre grains in austenitic stainless. Mater Sci Tech. 2017;33(4):480–486. doi: 10.1080/02670836.2016.1229092
23.
NezakatM, AkhianiH, HoseiniM, Effect of thermo-mechanical processing on texture evolution in austenitic stainless steel 316L. Mater Charact. 2014;98:10–17. doi: 10.1016/j.matchar.2014.10.006
24.
TokarskiT, CiosG, KulaA, High quality transmission Kikuchi diffraction analysis of deformed alloys - case study. Mater Charact. 2016;121:231–236. doi: 10.1016/j.matchar.2016.10.013
25.
SneddonGC, TrimbyPW, CairneyJM.Transmission Kikuchi diffraction in a scanning electron microscope: a review. Mat Sci Eng R. 2016;110:1–12. doi: 10.1016/j.mser.2016.10.001
26.
KurdjumowG, SachsG.Uber den Mechanismus der Stahlhartung. Z Phys. 1930;64:325–343. doi: 10.1007/BF01397346
27.
NishiyamaZ.X-ray investigation on the mechanism of the transformation from face-centered-cubic lattice to body-centered cubic lattice. Sci Rep Tohoku Univ. 1934;23:637–664.