A model for estimating the blocky retained austenite size distribution in Si-containing steels has been developed for the first time, based on the geometric partitioning of prior austenite grains by bainite sheaves. A random volume allocation method for the two new compartments formed by the formation of one bainite sheaf is adopted for reasons detailed in the text. Random selection of the compartment for subdivision is also employed at each step. The model has been verified experimentally using Si-containing bainitic steels.
CaballeroFG, BhadeshiaHKDH, MawellaKJA, et al. Very strong low temperature bainite. Mat Sci Technol. 2002;18(3):279–284. doi: 10.1179/026708301225000725
2.
CaballeroF, BhadeshiaH.Very strong bainite. Curr Opin Solid State Mater Sci. 2004;8(3):251–257. doi: 10.1016/j.cossms.2004.09.005
3.
MatsumuraO, SakumaY, TakechiH.Trip and its kinetic aspects in austempered 0.4 c-1.5 si-0.8 mn steel. Scr Metall. 1987;21(10):1301–1306. doi: 10.1016/0036-9748(87)90103-7
4.
SpeerJ, StreicherA, MatlockD, et al. Quenching and partitioning: a fundamentally new process to create high strength trip sheet microstructures. In: Symposium on the Thermodynamics, Kinetics, Characterization and Modeling of: Austenite Formation and Decomposition; 2003. p. 505–522.
5.
GrässelO, KrügerL, FrommeyerG, et al. High strength Fe–Mn–(Al, Si) TRIP/TWIP steels development - properties - application. Int J Plast. 2000;16(10):1391–1409. doi: 10.1016/S0749-6419(00)00015-2
6.
EdmondsD, HeK, RizzoF, et al. Quenching and partitioning martensite- novel steel heat treatment. Mater Sci Eng A. 2006;438:25–34. doi: 10.1016/j.msea.2006.02.133
7.
GiraultE, MertensA, JacquesP, et al. Comparison of the effects of silicon and aluminium on the tensile behaviour of multiphase TRIP-assisted steels. Scr Mater. 2001;44(6):885–892. doi: 10.1016/S1359-6462(00)00697-7
8.
BhadeshiaHKDH.Nanostructured bainite. Proc R Soc Lond A: Math Phys Eng Sci. 2009;466(2113):3–18.
9.
ChatterjeeS, BhadeshiaHKDH.TRIP-assisted steels: cracking of high-carbon martensite. Mater Sci Technol. 2006;22(6):645–649. doi: 10.1179/174328406X86182
10.
BhadeshiaHKDH, EdmondsDV.Bainite in silicon steels: new composition–property approach part 1. Metal Sci. 1983a;17(9):411–419. doi: 10.1179/030634583790420600
11.
BhadeshiaHKDH, EdmondsDV.Bainite in silicon steels: new composition–property approach part 2. Metal Sci. 1983b;17(9):420–425. doi: 10.1179/030634583790420646
12.
GuoL, RoelofsH, LembkeM, et al. Modelling of transition from upper to lower bainite in multi-component system. Mater Sci Technol. 2017a;33:430–437. doi: 10.1080/02670836.2016.1221495
13.
GuoL, RoelofsH, LembkeM, et al. Effect of manganese sulphide particle shape on the pinning of grain boundary'. Mater Sci Technol. 2017b;33:1013–1018. doi: 10.1080/02670836.2016.1258157
14.
GuoL, RoelofsH, LembkeM, et al. Modelling of recalescence effect on austenite decomposition. Mater Sci Technol. 2017c;33:1258–1267. doi: 10.1080/02670836.2017.1282693
15.
Pous-RomeroH, LonardelliI, CogswellD, et al. Austenite grain growth in a nuclear pressure vessel steel. Mater Sci Eng A. 2013;567:72–79. doi: 10.1016/j.msea.2013.01.005
16.
BhadeshiaH, DavidS, VitekJ, et al. Stress induced transformation to bainite in Fe–Cr–Mo–C pressure vessel steel. Mater Sci Technol. 1991;7(8):686–698. doi: 10.1179/mst.1991.7.8.686
FisherJC, HollomonJH, TurnbullD.Kinetics of the Austenite to Martensite Transformation. Metals Trans. 1949;185:691–700.
19.
GuimarãesJRC, RiosPR.Revisiting fisher's analysis of the martensite microstructure. Metall Mater Trans A. 2011;42:2937–2940. doi: 10.1007/s11661-011-0840-7
20.
MackC, BartlettMS.On clumps formed when convex laminae or bodies are placed at random in two or three dimensions. Math Proc Camb Philos Soc. 1956;52:246–250. doi: 10.1017/S0305004100031236
21.
ChangLC, BhadeshiaHKDH.Austenite films in bainitic microstructures. Mater Sci Technol. 1995;11(9):874–882. doi: 10.1179/mst.1995.11.9.874