Ultra-rapid microwave sintering of powder metals will provide fine microstructural features that improve mechanical properties. In present study, three grades of stainless steel powder compacts (316L, 430L, 410) were produced using a uniaxial compaction unit. These compacts were sintered by microwave hybrid heating method at 1300°C (super-solidus region). The densification response, microstructural attributes, and mechanical properties were compared at 30, 45 and 60 min holding times. The compositional analysis was performed with the help of optical emission spectroscopy (OES) and scanning electron microscopy equipped with energy dispersed spectroscopy(SEM-EDS). The results obtained from both spectroscopies are compared for the sintered samples. The correlation of mechanical properties is analysed with evolved microstructural attributes (pore volume, pore shape and pore distribution). The excellent strength of 457 ± 16 MPa, 466 ± 6 MPa and 476 ± 26 MPa with 23 ± 1.3%, 14 ± 1.5% and 11 ± 1% of ductility is observed for sintered AISI 316L, 430L and 410, respectively.
Shahabi KargarB, BabakhaniA, MoayedMH.Improving pore morphology of PM 316L stainless steels by prealloyed powder prepassivation in 20% nitric acid. Powder Metall. 2011;54(5):566–571. doi:10.1179/003258910X12827272082669.
2.
MartínF, GarcíaC, BlancoY, Influence of sinter-cooling rate on the mechanical properties of powder metallurgy austenitic, ferritic, and duplex stainless steels sintered in vacuum. Mater Sci Eng A. 2015;642:360–365. doi:10.1016/j.msea.2015.06.097.
BoillotP, PeultierJ.Use of stainless steels in the industry: recent and future developments. Procedia Eng. 2014;83:309–321. doi:10.1016/j.proeng.2014.09.015.
5.
KennedyS, KumaranS, Srinivasa RaoT.Microstructure and mechanical properties of microwave sintered austenitic stainless steel. Trans Indian Inst Met. 2011;64:85–87. doi:10.1007/s12666-011-0017-5.
6.
GabbitasBL, AriffTF, CaoP.Synthesis of pewter alloy from tin–copper– antimony powder mixtures by microwave and conventional sintering. Powder Metall. 2011;54:4. doi:10.1179/003258910X12680382874607.
7.
MolinariA, KaziorJ, MarchettiF, Sintering mechanisms of boron alloyed AISI 316L stainless steel. Powder Metall. 1994;37:115. doi:10.1179/pom.1994.37.2.115.
8.
WangWF, WuMJ.Effect of silicon content and aging time on density, hardness, toughness and corrosion resistance of sintered 303LSC–Si stainless steels. Mater Sci Eng A. 2006;425:167–171. doi:10.1016/j.msea.2006.03.050.
9.
MuthuchamyA, Raja AnnamalaiA, RankaR.Mechanical and Electrochemical Characterization of Super-Solidus Sintered Austenitic Stainless Steel (316L). High Temp Mater Process. 2015;35(7):643–651. doi:10.1515/htmp-20150083.
10.
Ramakrishna KandalaS, BalaniK, UpadhyayaA.Mechanical and Electrochemical Characterization of Super-Solidus Sintered Austenitic Stainless Steel (316L). High Temp Mater Process. 2019;38:792–805. doi:10.1515/htmp-2019-0032.
11.
PengZ, HwangJ-Y.Microwave-assisted metallurgy. Int Mater Rev. 2015;60(1):30–63. doi:10.1179/1743280414Y.0000000042.
12.
SunJ, WangW, YueQ.Review on microwave-matter interaction fundamentals and efficient microwave-associated heating strategies. Mater (Basel). 2016;9:231. doi:10.3390/ma9040231.
13.
RoyR, AgrawalDK, ChengJP, Full sintering of powdered-metal bodies in a microwave field. Nature. 1999;399:668. doi:10.1038/21390.
14.
AgrawalDK.Microwave processing of ceramics. Curr Opin Solid State Mater Sci. 1998;3(5):480–485. doi:10.1016/S1359-0286(98)80011-9.
15.
EbadzadehT, ValefiM.Microwave-assisted sintering of zircon. J Alloys Compd. 2008;448:246–249. doi:10.1016/j.jallcom.2007.02.032.
16.
AnklekarRM, BauerK, AgrawalDK, Improved mechanical properties and microstructural development of microwave sintered copper and nickel steel PM parts. Powder Metall. 2005;48(1):39–46. doi:10.1179/003258905X37657.
17.
Willert-PoradaM, ParkHS. In: ClarkDE, BinnerJGP, LewisDA, editor. Heating and sintering of steel powders with microwaves at 2.45GHz frequency- relationship between heating behavior and electrical conductivity. Microwaves: Theory and Application in Materials Processing-IV.The American Ceramic Society, Westerville, OH, USA, (IV); 2001. p. 459–470.
18.
PandaSS, SinghV, UpadhyayaA, Sintering response of austenitic (316L) and ferritic (434L) stainless steel consolidated in conventional and microwave furnaces. Scr Mater. 2006;54:2179–2183. doi:10.1016/j.scriptamat.2006.02.034.
19.
UsamentiagaR, VenegasP, GuerediagaJ, Infrared thermography for temperature measurement and Non-destructive testing. Sensors. 2014;14:12305–12348. doi:10.3390/s140712305.
20.
WenC-D, LuC-T.Suitability of multispectral radiation thermometry emissivity models for predicting steel surface temperature. J Thermophys Heat Trans. 2010;24(3):662–665. doi:10.2514/1.47810.
21.
Raja AnnamalaiA, UpadhyayalA, AgrawalDK.Effect of heating mode and electrochemical response on austenitic and ferritic stainless steels. Can Metall Q. 2015;54:142–148. doi:10.1179/1879139515Y.0000000001.
22.
RybakovKI, EgorovSV, EremeevAG, Ultra-rapid microwave sintering employing thermal instability and resonant absorption. J Mater Res. 2019: 1–15. doi:10.1557/jmr.2019.232.
23.
Veera Venkata NagarajuK, KumaranS, Srinivasa RaoT.Densification kinetics of P/M austenitic (316L) stainless steels processed by rapid microwave hybrid heating method at various conditions. Adv Mater Process Technol. 2021: 1–14. doi:10.1080/2374068X.2021.1970993.
24.
MishraRR, SharmaAK.Microwave heating characteristics of bulk metallic materials and role of oxides. J Mater Sci. 2018;53:567–584. doi:10.1007/s10853-018-2771-9.
25.
GermanRM. Powder Metallurgy and Particulate Materials Processing. Metal Powder Industries Federation, 105, College Road East, Princeton, New Jersey, 2005.
26.
Veera Venkata NagarajuK, KumaranS, Srinivasa RaoT.Electrochemical behavior of various grade P/M stainless steels processed by rapid microwave hybrid sintering (super-solidus) method. Mater Lett; 302:130394. doi:10.1016/j.matlet.2021.130394.
27.
WangH, ZhangY, ZhangY, Laboratory and numerical investigation of microwave heating properties of asphalt mixture. Materials (Basel). 2019;12:146. doi:10.3390/ma12010146.
28.
SantosT, CostaLC, ValenteM, 3D electromagnetic field simulation in microwave ovens: a tool to control thermal runaway. Proceedings of the 2015 COMSOL Conference in Grenoble.
29.
CuretS, Bellincanta BegniniF, RouaudO, Modeling microwave heating during batch processing of liquid sample in a single mode cavity. Proceedings of the 2015 COMSOL Conference in Grenoble.
30.
ManiereC, ZahrahT, EugeneA, Fully coupled electromagnetic-thermal-mechanical comparative simulation of direct vs hybrid microwave sintering of 3Y-ZrO2. J Am Ceram Soc. 2017;100:2439–2450. doi:10.1111/jace.14762.
31.
KennethCMILLS, YuchuSU, ZushuLI, Equations for the calculation of the thermo-physical properties of stainless steel. ISIJ Int. 2004;44(10):1661–1668.
32.
MartínF, GarcíaC, BlancoY, Influence of sinter cooling rate on the mechanical properties of powder metallurgy austenitic, ferritic and duplex stainless steels sintered in vacuum. Mater Sci Eng A. 2015;642:360–365. doi:10.1016/j.msea.2015.06.097.
33.
AkhtarF.Sintering behavior of elemental powders with FeB Addition in the composition of martensitic stainless steel. J Mat Eng Perf. 2007;16:726–729. doi:10.1007/s11665-007-9106-3.
34.
LopezD, FalleirosNA, TschiptschinAP.Corrosion–erosion behaviour of austenitic and martensitic high nitrogen stainless steels. Wear. 2007;263:347–354. doi:10.1016/j.wear.2007.01.053.
35.
YaoZ, XiongW, HuangB, Characteristics of 14Cr-ODS ferritic alloy fabricated by mechanically alloying and microwave sintering. J Nucl Mater. 2015;461:95–99. doi:10.1016/j.jnucmat.2015.01.030.
36.
BertilssonI, KarlssonB, IsenJ. J. Proceedings of the International Conference on MPIF, Toronto, 1994;16:19.