In order to increase the fatigue performance of mechanically loaded PM-components, case hardening procedures can be used to improve the surface layer states in terms of hardness and residual stress. In this work, the effects of carbonitriding treatment on two typical PM-steels with multiple densities are investigated in terms of their surface layer state (hardness, residual stress and retained austenite) before and after fatigue testing and their resulting pulsating fatigue performance. The results confirm fatigue strengths that can be formulated linearly as a function of porosity as well as a cyclic stability of the surface layer condition at loads below the fatigue strength. Further optimisation of the fatigue strength can be expected by tailoring the surface layer with respect to residual stresses. Comparisons to other studies are difficult due to many process parameters, different load cases and limited data, but indicate comparable fatigue strengths.
DanningerH, DlapkaM.Heat treatment of sintered steels – what is different?HTM. 2018;73(3):117–130. doi:10.3139/105.110353.
2.
DlapkaM, DanningerH, GierlC, Defining the pores in PM components. Met Powder Rep. 2010;65(2):30–33. doi:10.1016/S0026-0657(10)70093-X.
3.
HuppmannWJ, DalalK, WellnerP, Metallographic characterization of PM materials. Powder Metall. 1983;26(1):23–30. doi:10.1179/pom.1983.26.1.23.
4.
WidankaK.Effect of interconnected porosity on carbon diffusion depth in vacuum carburising process of iron compacts. Powder Metall. 2010;53(4):318–322. doi:10.1179/174329009X449332.
5.
DamonJM, SurmH, SaddeiP, Experimental and numerical investigation of the surface layer conditions after carbonitriding of powder metallurgical steels. part 1: diffusion in components of graded porosity. HTM. 2021;76(1):36–57. doi:10.1515/htm-2020-0003.
6.
NusskernP, HoffmeisterJ, SchulzeV.Powder metallurgical components: improvement of surface integrity by deep rolling and case hardening. Procedia CIRP. 2014;13:192–197. doi:10.1016/j.procir.2014.04.033.
7.
DIN EN ISO 3928:2017-03: Sintermetallwerkstoffe, ausgenommen Hartmetalle_- Probekörper für die Ermüdungsprüfung, DIN EN ISO, Berlin.
8.
SonsinoCM.Fatigue design for powder metallurgy. Powder Metall. 1990;33(3):235–245. doi:10.1179/pom.1990.33.3.235.
9.
HadrboletzA, WeissB.Fatigue behaviour of iron based sintered material: a review. Int Mater Rev. 1997;42(1):1–44. doi:10.1179/imr.1997.42.1.1.
10.
StraffeliniG, FontanariV, HafezA, Tensile and fatigue behaviour of sinter hardened Fe–1·5Mo–2Cu–0·6C steels. Powder Metall. 2009;52(4):298–303. doi:10.1179/003258909X12502679013774.
11.
SokolowskiP, LindsleyB.Leaner alloys for the PM industry. Powder Metall. 2012;55(2):84–87. doi:10.1179/0032589912Z.00000000054.
SeyediS. “Schwingfestigkeit einsatzgehärteter sinterstähle,” Dissertation2006, Institut für Angewandte Materialien, Universität Karlsruhe, Karlsruhe.
14.
VeigaA, Luno-BilbaoC, SainzS, Effect of low-pressure carburizing and plasma nitriding on mechanical properties and fatigue endurance limits of low alloy sintered steels. Powder Metall. 2020;63(2):75–79. doi:10.1080/00325899.2020.1758883.
15.
FaningerG, HartmannU.Physikalische grundlagen der quantitativen roentgenographischen phasenanalyse (RPA). Haert.-Tech. Mitt.1972;27:233–244.
16.
50100:2016: Schwingfestigkeitsversuch_- Durchführung und Auswertung von zyklischen Versuchen mit konstanter Lastamplitude für metallische Werkstoffproben und Bauteile, DIN, Berlin.
DamonJ, DietrichS, SchulzeV.Implications of carbon, nitrogen and porosity on the martensite phase transformation and resulting hardness in PM-steel Astaloy 85Mo. J Mater Res Tech. 2020;9(4):8245–8257. doi:10.1016/j.jmrt.2020.05.035.
19.
KlubbergF, SchaeferHJ, HempenM, Empirical relationship between pulsating And fully reversed fatigue strength amplitudes. WIT Trans Eng Sci. 2003;40: 255–365.
ZafariA, BeissP.Effect of tensile mean stresses on fatigue strength of fe-cu-c steels in as-sintered and heat treated conditions. Powder Metallurgy Progress. 2008;8(3):200.
22.
BeissP.Dauerfestigkeit von sinterwerkstoffen. Materwiss Werksttech. 1986;17(3):89–98.
23.
MerkelJ. “Untersuchungen zum Einfluss von Kugelstrahl- und Festwalzbehandlungen auf den Randschichtzustand und die Schwingfestigkeit von Sintereisenwerkstoffen,” Dissertation, Universität Karlsruhe, Karlsruhe, 2009. [Online]. Available: http://d-nb.info/992707765/04; http://d-nb.info/992707765/04.